Polymerizable absorbers of uv and high energy visible light

ABSTRACT

Described are polymerizable high energy light absorbing compounds. The compounds absorb various wavelengths of ultraviolet and/or high energy visible light and are suitable for incorporation in various products, such as biomedical devices and ophthalmic devices.

RELATED APPLICATIONS

This application claims priority to U.S. Provisional Patent ApplicationSer. No. 62/691,112, filed Jun. 28, 2018, and U.S. Provisional PatentApplication Ser. No. 62/637,505, filed Mar. 2, 2018, each of which isincorporated herein by reference in its entirety.

FIELD OF THE INVENTION

The invention relates to UV and high energy visible light absorbers.More particularly, the invention relates to compounds with polymerizablefunctionality that absorb various wavelengths of UV and/or high energyvisible light, and yet are visibly transparent when incorporated in anarticle. Thus, the compounds may be used in polymeric articles,including biomedical devices, such as ophthalmic devices.

BACKGROUND OF THE INVENTION

High energy light from the sun, such as UV light and high-energy visiblelight, is known to be responsible for cellular damage. While most of theradiation below 280 nm in wavelength is absorbed by the earth'satmosphere, photons possessing wavelengths ranging between 280 and 400nm have been associated with several ocular disorders including cornealdegenerative changes, and age-related cataract and macular degeneration.(See Statement on Ocular Ultraviolet Radiation Hazards in Sunlight,American Optometric Association, Nov. 10, 1993). The human corneaabsorbs some radiation up to 320 nm in wavelength (30% transmission)(Doutch, J. J., Quantock, A. J., Joyce, N. C., Meek, K. M, Biophys. J,2012, 102, 1258-1264), but is inefficient in protecting the back of theeye from radiation ranging from 320 to 400 nm in wavelength.

Contact lens standards define the upper UV radiation wavelength at 380nm. The current Class I UV absorbing criteria defined by the AmericanOptometric Association require >99% of the radiation between 280 and 315nm (UV B) and >90% of the 316 to 380 nm (UV A) radiation to be absorbedby the contact lens. While the criteria effectively address protectionof the cornea (<1% UV B transmittance), there is little attention paidto the lower energy UV radiation (>380 <400 nm) associated with retinaldamage (Ham, W. T, Mueller, H. A., Sliney, D. H. Nature 1976;260(5547):153-5) or to high energy visible radiation.

High energy-visible (HEV) radiation may cause visual discomfort orcircadian rhythm disruption. For example, computer and electronic devicescreens, flat screen televisions, energy efficient lights, and LEDlights are known to generate HEV light. Prolonged exposure to suchsources of HEV light may cause eye strain. Viewing HEV light emittingdevices at night is also postulated to disrupt the natural circadianrhythm leading, for example, to inadequate sleep.

Absorption of high energy light radiation before it reaches the eyecontinues to be a desirable goal in the ophthalmics field. However, theextent to which a particular wavelength range is absorbed is alsoimportant. For instance, in the UV A and UV B ranges, it may bedesirable to absorb as much radiation as possible. On the other hand,since HEV light forms a part of the visible spectrum, completeabsorption of HEV light may negatively affect vision. With HEV light,therefore, partial absorption may be more desirable.

There is a need for materials that provide targeted absorption ofundesirable wavelengths of high energy radiation, and that areprocessable into functional products. Compounds that absorb or attenuatehigh energy radiation, when used in ophthalmic devices, can help protectthe cornea, as well as the interior cells in the ocular environment,from degradation, strain, and/or circadian rhythm disruption.

SUMMARY OF THE INVENTION

The invention relates to high energy light absorbing compounds thatabsorb UV and/or high energy visible (HEV) light while substantiallytransmitting (e.g., greater than 80% transmission) at wavelengths longerthan about 450 nm. The compounds are therefore effective at providingtargeted absorption of high energy light, such as UV (UVA and UVB), lowenergy UV light (385 nm to 400 nm), or HEV light (e.g., 400 to 450 nm).

The compounds are also polymerizable and are generally compatible withother raw materials, as well as the polymerization and processingconditions that are typically used for making ophthalmic devices such assoft contact lenses. The compounds can therefore be readily covalentlyincorporated into the final product without the need for significantmodification of existing manufacturing processes and equipment.

Accordingly, in one aspect the invention provides a compound of formulaI:

wherein:

-   -   m and n are independently 0, 1, 2, 3, or 4;    -   T is a bond, O, or NR;    -   X is O, S, NR, SO, or SO₂;    -   Y is a linking group;    -   P_(g) is a polymerizable group;    -   R at each occurrence is independently H, C₁-C₆ alkyl,        cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or Y—P_(g);

R¹ and R², when present, are independently at each occurrence C₁-C₆alkyl, C₁-C₆ alkoxy, C₁-C₆ thioalkyl, C₃-C₇ cycloalkyl, aryl, halo,hydroxy, amino, NR³R⁴, or benzyl, wherein R³ and R⁴ are independently Hor C₁-C₆ alkyl, or two adjacent R¹ or R² groups, together with thecarbon atoms to which they are attached, combine to form a cycloalkyl oraryl ring; and

EWG is an electron withdrawing group, such as cyano, amide, ester, keto,or aldehyde (preferably cyano).

In another aspect, the invention provides an ophthalmic device that is afree radical reaction product of a reactive mixture comprising: one ormore monomers suitable for making the ophthalmic device; and apolymerizable high energy light absorbing compound comprising a compoundof formula I as described herein.

In a further aspect, the invention provides a method for making anophthalmic device. The method comprises: (a) providing a reactivemixture containing a compound of formula I as described herein, one ormore device forming monomers, and a radical initiator; and (b)polymerizing the reactive mixture to form the ophthalmic device.

In a still further aspect, the invention provides an ophthalmic devicethat is a reaction product of a reactive mixture comprising: apolymerizable high energy light absorbing compound; and one or moremonomers suitable for making an ophthalmic device, wherein theophthalmic device transmits: 45 percent or less of light having awavelength of 280 to 399 nm; from 1 percent to 70 percent of lighthaving a wavelength of 400 to 409 nm; and at least 80 percent of lighthaving a wavelength of 450 to 800 nm.

In a yet further aspect, the invention provides an ophthalmic devicethat is a polymerized reaction product of a reactive mixture comprisingone or more reactive components (such as a hydrophilic component and asilicone containing compound), wherein the polymerized reaction productcontains, as covalently bound substituents, one or more chromophores offormula IV:

wherein m, n, X, R¹, R², R⁵, and EWG are as defined herein.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 shows UV-VIS Transmission Spectra of 0.2 mM solutions ofexemplary Compounds (B), (C), and (E) in methanol.

FIG. 2 shows UV-VIS Transmission Spectra of 0.2 mM solutions ofCompounds (G), (H), and (J) in methanol and of Compound (L) indichloromethane

FIG. 3 shows UV-VIS Transmission Spectrum of exemplary Silicone HydrogelContact Lenses 9A and 9B.

FIG. 4 shows UV-VIS Transmission Spectrum of exemplary Silicone HydrogelContact Lenses 9A and 9C.

FIG. 5 shows UV-VIS Transmission Spectrum of exemplary Silicone HydrogelContact Lenses 9A and 9D.

FIG. 6 shows UV-VIS Transmission Spectrum of exemplary Silicone HydrogelContact Lenses 10A and 10B.

FIG. 7 shows UV-VIS Transmission Spectrum of exemplary Silicone HydrogelContact Lenses 10A and 10C.

FIG. 8 shows UV-VIS Transmission Spectrum of exemplary Silicone HydrogelContact Lenses 10A and 10B.

FIG. 9 shows UV-VIS Transmission Spectra of Silicone Hydrogel ContactLenses (11A) comprising Compound (B) after exposure to direct sunlight

FIG. 10 shows UV-VIS Transmission Spectra of Silicone Hydrogel ContactLenses (11B) comprising Compound (B) after exposure to indoor lighting

DETAILED DESCRIPTION OF THE INVENTION

It is to be understood that the invention is not limited to the detailsof construction or process steps set forth in the following description.The invention is capable of other embodiments and of being practiced orbeing carried out in various ways using the teaching herein.

As noted above, in one aspect, the invention provides UV/HEV absorbingcompounds. The compounds contain polymerizable functionality. It hasbeen discovered that ophthalmic devices that absorb substantial amountsof UV light as well as some amounts of HEV light can be readily preparedas described herein.

It has also been discovered that light absorbing compounds can beselected to provide targeted absorption of UV and/or high energy visiblelight (e.g., increased UV absorption and less HEV absorption, orincreased HEV absorption, etc.). Such targeting may be achieved, forexample, with compounds of formula I, which contain a hetero tricycliccore chromophore. For instance, as described in more detail below,compounds of formula I where the heteroatom (X in formula I) is sulfur,may absorb HEV light. On the other hand, compounds of formula I wherethe heteroatom is oxygen (X is O) may absorb less HEV light, but more UVlight. Thus, the compounds may be used to absorb select regions of UVand/or HEV light or they may be mixed together or with other absorbingcompounds to provide broad spectrum protection (e.g., UV and HEV light).Advantageously, the compounds exhibit a transmission cut-off (e.g., theyabsorb 20 percent or less) at visible wavelengths of 450 nm or longer.

It has further been discovered that compounds of formula I aresubstantially photostable, meaning that the compounds, when incorporatedin an ophthalmic device, do not undergo significant degradation overtime when exposed to lighting, such as indoor or outdoor lighting. Suchphotostability can be determined by measuring the UV/Vis transmissionspectrum of the ophthalmic device over a test period, such as 21 weeks.Significant changes in the spectrum over the test period are indicativeof a lack of photostability. By way of example, ophthalmic devices (suchas contact lenses) containing compounds of the invention, when exposedto indoor office lighting over a 21 week period at room temperature,exhibit 5% or less, preferable 2% or less, more preferably 0.5% or less,even more preferably 0.4% or less of change in their averagetransmission over a wavelength range of 380 to 700 nm. By way of furtherexample, ophthalmic devices (such as contact lenses) containingcompounds of the invention, when exposed to indoor office lighting overa 21 week period at room temperature, exhibit 5% or less, preferable 2%or less, more preferably 1% or less, even more preferably 0.7% or lessof change in their average transmission over a wavelength range of 400to 500 nm. Such changes may be calculated as the absolute value of thedifference between the average transmission (over the indicatedwavelength range) at time 21 weeks and at time zero.

Thus, compounds of the invention may successfully absorb UV (UVA, UVB),and/or HEV, while transmitting in the visible spectrum. The compoundsare suitable for incorporation in a variety of products, includingbiomedical devices and ophthalmic devices.

With respect to the terms used in this disclosure, the followingdefinitions are provided.

Unless defined otherwise, all technical and scientific terms used hereinhave the same meaning as commonly understood by one of ordinary skill inthe art to which the invention belongs. The polymer definitions areconsistent with those disclosed in the Compendium of Polymer Terminologyand Nomenclature, IUPAC Recommendations 2008, edited by: Richard G.Jones, Jaroslav Kahovec, Robert Stepto, Edward S. Wilks, Michael Hess,Tatsuki Kitayama, and W. Val Metanomski. All publications, patentapplications, patents, and other references mentioned herein areincorporated by reference.

As used herein, the term “(meth)” designates optional methylsubstitution. Thus, a term such as “(meth)acrylates” denotes bothmethacrylates and acrylates.

Wherever chemical structures are given, it should be appreciated thatalternatives disclosed for the substituents on the structure may becombined in any combination. Thus, if a structure contained substituentsR* and R**, each of which contained three lists of potential groups, 9combinations are disclosed. The same applies for combinations ofproperties.

When a subscript, such as “n” in the generic formula [***]_(n), is usedto depict the number of repeating units in a polymer's chemical formula,the formula should be interpreted to represent the number averagemolecular weight of the macromolecule.

The term “individual” includes humans and vertebrates.

The term “biomedical device” refers to any article that is designed tobe used while either in or on mammalian tissues or fluids, andpreferably in or on human tissue or fluids. Examples of these devicesinclude but are not limited to wound dressings, sealants, tissuefillers, drug delivery systems, coatings, adhesion prevention barriers,catheters, implants, stents, and ophthalmic devices such as intraocularlenses and contact lenses. The biomedical devices may be ophthalmicdevices, particularly contact lenses, most particularly contact lensesmade from silicone hydrogels or conventional hydrogels.

The term “ocular surface” includes the surface and glandular epitheliaof the cornea, conjunctiva, lacrimal gland, accessory lacrimal glands,nasolacrimal duct and meibomian gland, and their apical and basalmatrices, puncta and adjacent or related structures, including eyelidslinked as a functional system by both continuity of epithelia, byinnervation, and the endocrine and immune systems.

The term “ophthalmic device” refers to any device which resides in or onthe eye or any part of the eye, including the ocular surface. Thesedevices can provide optical correction, cosmetic enhancement, visionenhancement, therapeutic benefit (for example as bandages) or deliveryof active components such as pharmaceutical and nutraceuticalcomponents, or a combination of any of the foregoing. Examples ofophthalmic devices include but are not limited to lenses, optical andocular inserts, including but not limited to punctal plugs, and thelike. “Lenses” include soft contact lenses, hard contact lenses, hybridcontact lenses, intraocular lenses, and overlay lenses. The ophthalmicdevice may comprise a contact lens.

The term “contact lens” refers to an ophthalmic device that can beplaced on the cornea of an individual's eye. The contact lens mayprovide corrective, cosmetic, or therapeutic benefit, including woundhealing, the delivery of drugs or nutraceuticals, diagnostic evaluationor monitoring, ultraviolet light absorbing, visible light or glarereduction, or any combination thereof. A contact lens can be of anyappropriate material known in the art and can be a soft lens, a hardlens, or a hybrid lens containing at least two distinct portions withdifferent physical, mechanical, or optical properties, such as modulus,water content, light transmission, or combinations thereof.

The biomedical devices, ophthalmic devices, and lenses of the presentinvention may be comprised of silicone hydrogels or conventionalhydrogels. Silicone hydrogels typically contain at least one hydrophilicmonomer and at least one silicone-containing component that arecovalently bound to one another in the cured device.

“Target macromolecule” means the macromolecule being synthesized fromthe reactive monomer mixture comprising monomers, macromers,prepolymers, cross-linkers, initiators, additives, diluents, and thelike.

The term “polymerizable compound” means a compound containing one ormore polymerizable groups. The term encompasses, for instance, monomers,macromers, oligomers, prepolymers, cross-linkers, and the like.

“Polymerizable groups” are groups that can undergo chain growthpolymerization, such as free radical and/or cationic polymerization, forexample a carbon-carbon double bond which can polymerize when subjectedto radical polymerization initiation conditions. Non-limiting examplesof free radical polymerizable groups include (meth)acrylates, styrenes,vinyl ethers, (meth)acrylamides, N-vinyllactams, N-vinylamides,O-vinylcarbamates, O-vinylcarbonates, and other vinyl groups.Preferably, the free radical polymerizable groups comprise(meth)acrylate, (meth)acrylamide, N-vinyl lactam, N-vinylamide, andstyryl functional groups, and mixtures of any of the foregoing. Morepreferably, the free radical polymerizable groups comprise(meth)acrylates, (meth)acrylamides, and mixtures thereof. Thepolymerizable group may be unsubstituted or substituted. For instance,the nitrogen atom in (meth)acrylamide may be bonded to a hydrogen, orthe hydrogen may be replaced with alkyl or cycloalkyl (which themselvesmay be further substituted).

Any type of free radical polymerization may be used including but notlimited to bulk, solution, suspension, and emulsion as well as any ofthe controlled radical polymerization methods such as stable freeradical polymerization, nitroxide-mediated living polymerization, atomtransfer radical polymerization, reversible addition fragmentation chaintransfer polymerization, organotellurium mediated living radicalpolymerization, and the like.

A “monomer” is a mono-functional molecule which can undergo chain growthpolymerization, and in particular, free radical polymerization, therebycreating a repeating unit in the chemical structure of the targetmacromolecule. Some monomers have di-functional impurities that can actas cross-linking agents. A “hydrophilic monomer” is also a monomer whichyields a clear single phase solution when mixed with deionized water at25° C. at a concentration of 5 weight percent. A “hydrophilic component”is a monomer, macromer, prepolymer, initiator, cross-linker, additive,or polymer which yields a clear single phase solution when mixed withdeionized water at 25° C. at a concentration of 5 weight percent. A“hydrophobic component” is a monomer, macromer, prepolymer, initiator,cross-linker, additive, or polymer which is slightly soluble orinsoluble in deionized water at 25° C.

A “macromolecule” is an organic compound having a number averagemolecular weight of greater than 1500, and may be reactive ornon-reactive.

A “macromonomer” or “macromer” is a macromolecule that has one groupthat can undergo chain growth polymerization, and in particular, freeradical polymerization, thereby creating a repeating unit in thechemical structure of the target macromolecule. Typically, the chemicalstructure of the macromer is different than the chemical structure ofthe target macromolecule, that is, the repeating unit of the macromer'spendent group is different than the repeating unit of the targetmacromolecule or its mainchain. The difference between a monomer and amacromer is merely one of chemical structure, molecular weight, andmolecular weight distribution of the pendent group. As a result, and asused herein, the patent literature occasionally defines monomers aspolymerizable compounds having relatively low molecular weights of about1,500 Daltons or less, which inherently includes some macromers. Inparticular, monomethacryloxypropyl terminated mono-n-butyl terminatedpolydimethylsiloxane (molecular weight=500-1500 g/mol) (mPDMS) andmono-(2-hydroxy-3-methacryloxypropyl)-propyl ether terminatedmono-n-butyl terminated polydimethylsiloxane (molecular weight=500-1500g/mol) (OH-mPDMS) may be referred to as monomers or macromers.Furthermore, the patent literature occasionally defines macromers ashaving one or more polymerizable groups, essentially broadening thecommon definition of macromer to include prepolymers. As a result and asused herein, di-functional and multi-functional macromers, prepolymers,and crosslinkers may be used interchangeably.

A “silicone-containing component” is a monomer, macromer, prepolymer,cross-linker, initiator, additive, or polymer in the reactive mixturewith at least one silicon-oxygen bond, typically in the form of siloxygroups, siloxane groups, carbosiloxane groups, and mixtures thereof.

Examples of silicone-containing components which are useful in thisinvention may be found in U.S. Pat. Nos. 3,808,178, 4,120,570,4,136,250, 4,153,641, 4,740,533, 5,034,461, 5,070,215, 5,244,981,5,314,960, 5,331,067, 5,371,147, 5,760,100, 5,849,811, 5,962,548,5,965,631, 5,998,498, 6,367,929, 6,822,016, 6,943,203, 6,951,894,7,052,131, 7,247,692, 7,396,890, 7,461,937, 7,468,398, 7,538,146,7,553,880, 7,572,841, 7,666,921, 7,691,916, 7,786,185, 7,825,170,7,915,323, 7,994,356, 8,022,158, 8,163,206, 8,273,802, 8,399,538,8,415,404, 8,420,711, 8,450,387, 8,487,058, 8,568,626, 8,937,110,8,937,111, 8,940,812, 8,980,972, 9,056,878, 9,125,808, 9,140,825,9,156,934, 9,170,349, 9,217,813, 9,244,196, 9,244,197, 9,260,544,9,297,928, 9,297,929, and European Patent No. 080539. These patents arehereby incorporated by reference in their entireties.

A “polymer” is a target macromolecule composed of the repeating units ofthe monomers used during polymerization.

A “homopolymer” is a polymer made from one monomer; a “copolymer” is apolymer made from two or more monomers; a “terpolymer” is a polymer madefrom three monomers. A “block copolymer” is composed of compositionallydifferent blocks or segments. Diblock copolymers have two blocks.Triblock copolymers have three blocks. “Comb or graft copolymers” aremade from at least one macromer.

A “repeating unit” is the smallest group of atoms in a polymer thatcorresponds to the polymerization of a specific monomer or macromer.

An “initiator” is a molecule that can decompose into radicals which cansubsequently react with a monomer to initiate a free radicalpolymerization reaction. A thermal initiator decomposes at a certainrate depending on the temperature; typical examples are azo compoundssuch as 1,1′-azobisisobutyronitrile and 4,4′-azobis(4-cyanovalericacid), peroxides such as benzoyl peroxide, tert-butyl peroxide,tert-butyl hydroperoxide, tert-butyl peroxybenzoate, dicumyl peroxide,and lauroyl peroxide, peracids such as peracetic acid and potassiumpersulfate as well as various redox systems. A photo-initiatordecomposes by a photochemical process; typical examples are derivativesof benzil, benzoin, acetophenone, benzophenone, camphorquinone, andmixtures thereof as well as various monoacyl and bisacyl phosphineoxides and combinations thereof.

A “cross-linking agent” is a di-functional or multi-functional monomeror macromer which can undergo free radical polymerization at two or morelocations on the molecule, thereby creating branch points and apolymeric network. Common examples are ethylene glycol dimethacrylate,tetraethylene glycol dimethacrylate, trimethylolpropane trimethacrylate,methylene bisacrylamide, triallyl cyanurate, and the like.

A “prepolymer” is a reaction product of monomers which containsremaining polymerizable groups capable of undergoing further reaction toform a polymer.

A “polymeric network” is a cross-linked macromolecule that can swell butcannot dissolve in solvents. “Hydrogels” are polymeric networks thatswell in water or aqueous solutions, typically absorbing at least 10weight percent water. “Silicone hydrogels” are hydrogels that are madefrom at least one silicone-containing component with at least onehydrophilic component. Hydrophilic components may also includenon-reactive polymers.

“Conventional hydrogels” refer to polymeric networks made fromcomponents without any siloxy, siloxane or carbosiloxane groups.Conventional hydrogels are prepared from reactive mixtures comprisinghydrophilic monomers. Examples include 2-hydroxyethyl methacrylate(“HEMA”), N-vinyl pyrrolidone (“NVP”), N, N-dimethylacrylamide (“DMA”)or vinyl acetate. U.S. Pat. Nos. 4,436,887, 4,495,313, 4,889,664,5,006,622, 5,039459, 5,236,969, 5,270,418, 5,298,533, 5,824,719,6,420,453, 6,423,761, 6,767,979, 7,934,830, 8,138,290, and 8,389,597disclose the formation of conventional hydrogels. Commercially availableconventional hydrogels include, but are not limited to, etafilcon,genfilcon, hilafilcon, lenefilcon, nesofilcon, omafilcon, polymacon, andvifilcon, including all of their variants.

“Silicone hydrogels” refer to polymeric networks made from at least onehydrophilic component and at least one silicone-containing component.Examples of silicone hydrogels include acquafilcon, asmofilcon,balafilcon, comfilcon, delefilcon, enfilcon, fanfilcon, formofilcon,galyfilcon, lotrafilcon, narafilcon, riofilcon, samfilcon, senofilcon,somofilcon, and stenfilcon, including all of their variants, as well assilicone hydrogels as prepared in U.S. Pat. Nos. 4,659,782, 4,659,783,5,244,981, 5,314,960, 5,331,067, 5,371,147, 5,998,498, 6,087,415,5,760,100, 5,776,999, 5,789,461, 5,849,811, 5,965,631, 6,367,929,6,822,016, 6,867,245, 6,943,203, 7,247,692, 7,249,848, 7,553,880,7,666,921, 7,786,185, 7,956,131, 8,022,158, 8,273,802, 8,399,538,8,470,906, 8,450,387, 8,487,058, 8,507,577, 8,637,621, 8,703,891,8,937,110, 8,937,111, 8,940,812, 9,056,878, 9,057,821, 9,125,808,9,140,825, 9156,934, 9,170,349, 9,244,196, 9,244,197, 9,260,544,9,297,928, 9,297,929 as well as WO 03/22321, WO 2008/061992, and US2010/0048847. These patents are hereby incorporated by reference intheir entireties.

An “interpenetrating polymeric network” comprises two or more networkswhich are at least partially interlaced on the molecular scale but notcovalently bonded to each other and which cannot be separated withoutbraking chemical bonds. A “semi-interpenetrating polymeric network”comprises one or more networks and one or more polymers characterized bysome mixing on the molecular level between at least one network and atleast one polymer. A mixture of different polymers is a “polymer blend.”A semi-interpenetrating network is technically a polymer blend, but insome cases, the polymers are so entangled that they cannot be readilyremoved.

The terms “reactive mixture” and “reactive monomer mixture” refer to themixture of components (both reactive and non-reactive) which are mixedtogether and, when subjected to polymerization conditions, form theconventional or silicone hydrogels of the present invention as well asbiomedical devices, ophthalmic devices, and contact lenses madetherefrom. The reactive monomer mixture may comprise reactive componentssuch as the monomers, macromers, prepolymers, cross-linkers, andinitiators, additives such as wetting agents, polymers, dyes, lightabsorbing compounds such as UV absorbers, pigments, dyes andphotochromic compounds, any of which may be reactive or non-reactive butare capable of being retained within the resulting biomedical device, aswell as pharmaceutical and nutraceutical compounds, and any diluents. Itwill be appreciated that a wide range of additives may be added basedupon the biomedical device which is made and its intended use.Concentrations of components of the reactive mixture are expressed asweight percentages of all components in the reactive mixture, excludingdiluent. When diluents are used, their concentrations are expressed asweight percentages based upon the amount of all components in thereactive mixture and the diluent.

“Reactive components” are the components in the reactive mixture whichbecome part of the chemical structure of the polymeric network of theresulting hydrogel by covalent bonding, hydrogen bonding, electrostaticinteractions, the formation of interpenetrating polymeric networks, orany other means.

The term “silicone hydrogel contact lens” refers to a hydrogel contactlens that is made from at least one silicone-containing compound.Silicone hydrogel contact lenses generally have increased oxygenpermeability compared to conventional hydrogels. Silicone hydrogelcontact lenses use both their water and polymer content to transmitoxygen to the eye.

The term “multi-functional” refers to a component having two or morepolymerizable groups. The term “mono-functional” refers to a componenthaving one polymerizable group.

The terms “halogen” or “halo” indicate fluorine, chlorine, bromine, andiodine.

“Alkyl” refers to an optionally substituted linear or branched alkylgroup containing the indicated number of carbon atoms. If no number isindicated, then alkyl (including any optional substituents on alkyl) maycontain 1 to 16 carbon atoms. Preferably, the alkyl group contains 1 to10 carbon atoms, alternatively 1 to 8 carbon atoms, alternatively 1 to 6carbon atoms, or alternatively 1 to 4 carbon atoms. Examples of alkylinclude methyl, ethyl, propyl, isopropyl, butyl, iso-, sec- andtert-butyl, pentyl, hexyl, heptyl, 3-ethylbutyl, and the like. Examplesof substituents on alkyl include 1, 2, or 3 groups independentlyselected from hydroxy, amino, amido, oxa, carboxy, alkyl carboxy,carbonyl, alkoxy, thioalkyl, carbamate, carbonate, halogen, phenyl,benzyl, and combinations thereof. “Alkylene” means a divalent alkylgroup, such as —CH₂—, —CH₂CH₂—, —CH₂CH₂CH₂—, —CH₂CH(CH₃)CH₂—, and—CH₂CH₂CH₂CH₂—.

“Haloalkyl” refers to an alkyl group as defined above substituted withone or more halogen atoms, where each halogen is independently F, Cl, Bror I. A preferred halogen is F. Preferred haloalkyl groups contain 1-6carbons, more preferably 1-4 carbons, and still more preferably 1-2carbons. “Haloalkyl” includes perhaloalkyl groups, such as —CF₃— or—CF₂CF₃—. “Haloalkylene” means a divalent haloalkyl group, such as—CH₂CF₂—.

“Cycloalkyl” refers to an optionally substituted cyclic hydrocarboncontaining the indicated number of ring carbon atoms. If no number isindicated, then cycloalkyl may contain 3 to 12 ring carbon atoms.Preferred are C₃-C₈ cycloalkyl groups, C₃-C₇ cycloalkyl, more preferablyC₄-C₇ cycloalkyl, and still more preferably C₅-C₆ cycloalkyl. Examplesof cycloalkyl include cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl,cycloheptyl and cyclooctyl. Examples of substituents on cycloalkylinclude 1, 2, or 3 groups independently selected from alkyl, hydroxy,amino, amido, oxa, carbonyl, alkoxy, thioalkyl, amido, carbamate,carbonate, halo, phenyl, benzyl, and combinations thereof.“Cycloalkylene” means a divalent cycloalkyl group, such as1,2-cyclohexylene, 1,3-cyclohexylene, or 1,4-cyclohexylene.

“Heterocycloalkyl” refers to a cycloalkyl ring or ring system as definedabove in which at least one ring carbon has been replaced with aheteroatom selected from nitrogen, oxygen, and sulfur. Theheterocycloalkyl ring is optionally fused to or otherwise attached toother heterocycloalkyl rings and/or non-aromatic hydrocarbon ringsand/or phenyl rings. Preferred heterocycloalkyl groups have from 5 to 7members. More preferred heterocycloalkyl groups have 5 or 6 members.Heterocycloalkylene means a divalent heterocycloalkyl group.

“Aryl” refers to an optionally substituted aromatic hydrocarbon ringsystem containing at least one aromatic ring. The aryl group containsthe indicated number of ring carbon atoms. If no number is indicated,then aryl may contain 6 to 14 ring carbon atoms. The aromatic ring mayoptionally be fused or otherwise attached to other aromatic hydrocarbonrings or non-aromatic hydrocarbon rings. Examples of aryl groups includephenyl, naphthyl, and biphenyl. Preferred examples of aryl groupsinclude phenyl. Examples of substituents on aryl include 1, 2, or 3groups independently selected from alkyl, hydroxy, amino, amido, oxa,carboxy, alkyl carboxy, carbonyl, alkoxy, thioalkyl, carbamate,carbonate, halo, phenyl, benzyl, and combinations thereof. “Arylene”means a divalent aryl group, for example 1,2-phenylene, 1,3-phenylene,or 1,4-phenylene.

“Heteroaryl” refers to an aryl ring or ring system, as defined above, inwhich at least one ring carbon atom has been replaced with a heteroatomselected from nitrogen, oxygen, and sulfur. The heteroaryl ring may befused or otherwise attached to one or more heteroaryl rings, aromatic ornonaromatic hydrocarbon rings or heterocycloalkyl rings. Examples ofheteroaryl groups include pyridyl, furyl, and thienyl. “Heteroarylene”means a divalent heteroaryl group.

“Alkoxy” refers to an alkyl group attached to the parent molecularmoiety through an oxygen bridge. Examples of alkoxy groups include, forinstance, methoxy, ethoxy, propoxy and isopropoxy. “Thioalkyl” means analkyl group attached to the parent molecule through a sulfur bridge.Examples of thioalkyl groups include, for instance, methylthio,ethylthio, n-propylthio and iso-propylthio. “Aryloxy” refers to an arylgroup attached to a parent molecular moiety through an oxygen bridge.Examples include phenoxy. “Cyclic alkoxy” means a cycloalkyl groupattached to the parent moiety through an oxygen bridge.

“Alkylamine” refers to an alkyl group attached to the parent molecularmoiety through an —NH bridge. Alkyleneamine means a divalent alkylaminegroup, such as —CH₂CH₂NH—.

“Siloxanyl” refers to a structure having at least one Si—O—Si bond.Thus, for example, siloxanyl group means a group having at least oneSi—O—Si group (i.e. a siloxane group), and siloxanyl compound means acompound having at least one Si—O—Si group. “Siloxanyl” encompassesmonomeric (e.g., Si—O—Si) as well as oligomeric/polymeric structures(e.g., —[Si—O]_(n)—, where n is 2 or more). Each silicon atom in thesiloxanyl group is substituted with independently selected R^(A) groups(where R^(A) is as defined in formula A options (b)-(i)) to completetheir valence.

“Silyl” refers to a structure of formula R₃Si— and “siloxy” refers to astructure of formula R₃Si—O—, where each R in silyl or siloxy isindependently selected from trimethylsiloxy, C₁-C₈ alkyl (preferablyC₁-C₃ alkyl, more preferably ethyl or methyl), and C₃-C₈ cycloalkyl.

“Alkyleneoxy” refers to groups of the general formula -(alkylene-O)_(p)—or —(O-alkylene)_(p)-, wherein alkylene is as defined above, and p isfrom 1 to 200, or from 1 to 100, or from 1 to 50, or from 1 to 25, orfrom 1 to 20, or from 1 to 10, wherein each alkylene is independentlyoptionally substituted with one or more groups independently selectedfrom hydroxyl, halo (e.g., fluoro), amino, amido, ether, carbonyl,carboxyl, and combinations thereof. If p is greater than 1, then eachalkylene may be the same or different and the alkyleneoxy may be inblock or random configuration. When alkyleneoxy forms a terminal groupin a molecule, the terminal end of the alkyleneoxy may, for instance, bea hydroxy or alkoxy (e.g., HO—[CH₂CH₂O]_(p)— or CH₃O—[CH₂CH₂O]_(p)—).Examples of alkyleneoxy include polyethyleneoxy, polypropyleneoxy,polybutyleneoxy, and poly(ethyleneoxy-co-propyleneoxy).

“Oxaalkylene” refers to an alkylene group as defined above where one ormore non-adjacent CH₂ groups have been substituted with an oxygen atom,such as —CH₂CH₂OCH(CH₃)CH₂—. “Thiaalkylene” refers to an alkylene groupas defined above where one or more non-adjacent CH₂ groups have beensubstituted with a sulfur atom, such as —CH₂CH₂SCH(CH₃)CH₂—.

The term “linking group” refers to a moiety that links a polymerizablegroup to the parent molecule. The linking group may be any moiety thatis compatible with the compound of which it is a part, and that does notundesirably interfere with the polymerization of the compound, is stableunder the polymerization conditions as well as the conditions for theprocessing and storage of the final product. For instance, the linkinggroup may be a bond, or it may comprise one or more alkylene,haloalkylene, amide, amine, alkyleneamine, carbamate, ester (—CO₂—),arylene, heteroarylene, cycloalkylene, heterocycloalkylene, alkyleneoxy,oxaalkylene, thiaalkylene, haloalkyleneoxy (alkyleneoxy substituted withone or more halo groups, e.g., —OCF₂—, —OCF₂CF₂—, —OCF₂CH₂—), siloxanyl,alkylenesiloxanyl, or combinations thereof. The linking group mayoptionally be substituted with 1 or more substituent groups. Suitablesubstituent groups may include those independently selected from alkyl,halo (e.g., fluoro), hydroxyl, HO-alkyleneoxy, MeO-alkyleneoxy,siloxanyl, siloxy, siloxy-alkyleneoxy-, siloxy-alkylene-alkyleneoxy-(where more than one alkyleneoxy groups may be present and wherein eachmethylene in alkylene and alkyleneoxy is independently optionallysubstituted with hydroxyl), ether, amine, carbonyl, carbamate, andcombinations thereof. The linking group may also be substituted with apolymerizable group, such as (meth)acrylate (in addition to thepolymerizable group to which the linking group is linked).

Preferred linking groups include C₁-C₈ alkylene (preferably C₂-C₆alkylene) and C₁-C₈ oxaalkylene (preferably C₂-C₆ oxaalkylene), each ofwhich is optionally substituted with 1 or 2 groups independentlyselected from hydroxyl and siloxy. Preferred linking groups also includecarboxylate, amide, C₁-C₈ alkylene-carboxylate-C₁-C₈ alkylene, or C₁-C₈alkylene-amide-C₁-C₈ alkylene.

When the linking group is comprised of combinations of moieties asdescribed above (e.g., alkylene and cycloalkylene), the moieties may bepresent in any order. For instance, if in Formula E below, L isindicated as being -alkylene-cycloalkylene-, then Rg-L may be eitherRg-alkylene-cycloalkylene-, or Rg-cycloalkylene-alkylene-.Notwithstanding this, the listing order represents the preferred orderin which the moieties appear in the compound starting from the terminalpolymerizable group (Rg or Pg) to which the linking group is attached.For example, if in Formula E, L and L² are indicated as both beingalkylene-cycloalkylene, then Rg-L is preferablyRg-alkylene-cycloalkylene- and -L²-Rg is preferably-cycloalkylene-alkylene-Rg.

The term “electron withdrawing group” (EWG) refers to a chemical groupwhich withdraws electron density from the atom or group of atoms towhich the electron withdrawing group is attached. Examples of EWGsinclude, but are not limited to, cyano, amide, ester, keto, or aldehyde.A preferred EWG is cyano (CN).

The terms “high energy radiation absorber,” “UV/HEV absorber,” or “highenergy light absorbing compound” refer to chemical materials that absorbvarious wavelengths of ultraviolet light, high energy visible light, orboth. A material's ability to absorb certain wavelengths of light can bedetermined by measuring its UV/Vis transmission spectrum. Compounds thatexhibit no absorption at a particular wavelength will exhibitsubstantially 100 percent transmission at that wavelength. Conversely,compounds that completely absorb at a particular wavelength will exhibitsubstantially 0% transmission at that wavelength. If the amount of amaterial's transmission is indicated as a percentage for a particularwavelength range, it is to be understood that the material exhibits thepercent transmission at all wavelengths within that range.

Unless otherwise indicated, ratios, percentages, parts, and the like areby weight.

Unless otherwise indicated, numeric ranges, for instance as in “from 2to 10,” are inclusive of the numbers defining the range (e.g., 2 and10).

As noted above, one aspect the invention provides an ophthalmic devicethat is a reaction product of a reactive mixture comprising: one or morepolymerizable high energy light absorbing compounds and one or moremonomers suitable for making an ophthalmic device, wherein theophthalmic device transmits: 45 percent or less of light having awavelength of 280 to 399 nm; at least 1 percent and up to 70 percent oflight having a wavelength of 400 to 409 nm; and at least 80 percent oflight having a wavelength of 450 to 800 nm. Preferably the ophthalmicdevice also transmits at least 10 percent and up to 95 percent of lighthaving a wavelength of 410 to 424 nm. Also preferably, the ophthalmicdevice transmits at least 50 percent of light having a wavelength of 425to 449 nm. Further preferably, the ophthalmic device transmits 10percent or less of light having a wavelength of 200 to 279 nm.

Preferably, the transmission of the ophthalmic device at 200 to 279 nmis 5 percent or less or 1 percent or less. Or preferably it is less than1 percent.

Preferably, the transmission of the ophthalmic device at 280 to 399 nmis 35 percent or less, or 25 percent or less, or 20 percent or less, or10 percent or less, or 5 percent or less, or 1 percent or less.

Preferably, the transmission of the ophthalmic device at 400 to 409 nmis at least 2 percent, at least 3 percent, or at least 4 percent. Alsopreferably, the transmission of the ophthalmic device at 400 to 409 nmis up to 60 percent, or up to 50 percent, or up to 40 percent, or up to30 percent, or up 20 percent.

Preferably, the transmission of the ophthalmic device at 410 to 424 nmis at least 15 percent. Also preferably, the transmission of theophthalmic device at 410 to 424 nm is up to 85 percent, up to 75percent, or up 65 percent.

Preferably, the transmission of the ophthalmic device at 425 to 449 nmis at least 60 percent.

Preferably, the transmission of the ophthalmic device at 450 to 800 nmis at least 85 percent.

Preferred ophthalmic devices are contact lenses, more preferably softhydrogel contact lenses. The foregoing transmission wavelengths andpercentages may be measured on various thicknesses of lenses. Forexample, the center thickness may be from 80 to 100 microns, or from 90to 100 microns or from 90 to 95 microns. Various concentrations of theone or more polymerizable high energy light absorbing compounds may beused to achieve the foregoing results. For instance, the concentrationmay be in the range of at least 0.1 percent or at least 2 percent; andup to 10 percent or up to 5 percent, based on the weight percentages ofall components in the reactive mixture, excluding diluent. A typicalconcentration may be in the range of 1 to 5 percent.

The invention also provides UV/HEV absorbing compounds of formula I:

wherein:

-   -   m and n are independently 0, 1, 2, 3, or 4;    -   T is a bond, O, or NR;    -   X is O, S, NR, SO, or SO₂;    -   Y is a linking group;    -   P_(g) is a polymerizable group;    -   R at each occurrence is independently H, C₁-C₆ alkyl,        cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or Y—P_(g);    -   R¹ and R², when present, are independently at each occurrence        C₁-C₆ alkyl, C₁-C₆ alkoxy, C₁-C₆ thioalkyl, C₃-C₇ cycloalkyl,        aryl (preferably unsubstituted phenyl or phenyl substituted with        alkyl or halo), halo, hydroxy, amino, NR³R⁴, or benzyl, wherein        R³ and R⁴ are independently H or C₁-C₆ alkyl, or two adjacent R¹        or R² groups, together with the carbon atoms to which they are        attached, combine to form a cycloalkyl or aryl ring; and

EWG is an electron withdrawing group.

Compounds of formula I preferably contain one or two Y—P_(g) groups.More preferably, the compounds contain one Y—P_(g) group.

Formula I-1. Compounds of formula I may include compounds of formulaI-1, which are compounds of formula I wherein X is S.

I-2. Compounds of formula I may include compounds of formula I-2, whichare compounds of formula I wherein X is O.

I-3. Compounds of formula I may include compounds of formula I-3, whichare compounds of formula I wherein X is NR, preferably NH or N-alkyl.

I-4. Compounds of formula I may include compounds of formula I-4, whichare compounds of formula I wherein X is SO.

I-5. Compounds of formula I may include compounds of formula I-5, whichare compounds of formula I wherein X is SO₂.

I-6. Compounds of formulae I, I-1, I-2, I-3, I-4, and I-5 may includecompounds of formula I-6, which are compounds of formula I, I-1, I-2,I-3, I-4, or I-5 wherein m and n are independently 0 or 1, oralternatively both are 0.

I-7. Compounds of formulae I, I-1, I-2, I-3, I-4, and I-5 may includecompounds of formula I-7, which are compounds of formula I, I-1, I-2,I-3, I-4, or I-5 wherein m is 1 and R¹ is C₁-C₆ alkyl, preferably ethylor methyl.

I-8. Compounds of formulae I, I-1, I-2, I-3, I-4, I-5, and I-7 mayinclude compounds of formula I-8, which are compounds of formula I, I-1,I-2, I-3, I-4, I-5, or I-7 wherein n is 1 and R² is C₁-C₆ alkyl,preferably ethyl or methyl.

I-9. Compounds of formulae I, I-1, I-2, I-3, I-4, I-5, I-6, I-7 and I-8may include compounds of formula I-9, which are compounds of formula I,I-1, I-2, I-3, I-4, I-5, I-6, I-7 or I-8 wherein R is H, or C₁-C₆ alkyl.Preferably, R in the group T is H.

I-10. Compounds of formulae I, I-1, I-2, I-3, I-4, I-5, I-6, I-7, I-8,and I-9 may include compounds of formula I-10, which are compounds offormula I, I-1, I-2, I-3, I-4, I-5, I-6, I-7, I-8, or I-9 wherein P_(g)(a polymerizable group) at each occurrence independently comprisesstyryl, vinyl carbonate, vinyl ether, vinyl carbamate, N-vinyl lactam,N-vinylamide, (meth)acrylate, or (meth)acrylamide. The polymerizablegroup allows the compounds of the invention to form covalent bonds whenreacted with monomers, crosslinking agents, and other componentsgenerally used in making polymeric devices. The compatibility of thecompounds with the reactive mixture can be controlled via the selectionof the polymerizable group (and the linking group). Preferredpolymerizable groups include (meth)acrylate or (meth)acrylamide. A morepreferred polymerizable group is methacrylate.

I-11. Compounds of formulae I, I-1, I-2, I-3, I-4, I-5, I-6, I-7, I-8,I-9, and I-10 may include compounds of formula I-11, which are compoundsof formula I, I-1, I-2, I-3, I-4, I-5, I-6, I-7, I-8, I-9, or I-10wherein Y (a linking group) is alkylene, cycloalkylene,heterocycloalkylene, arylene (e.g., phenylene), heteroarylene,oxaalkylene, alkylene-amide-alkylene, alkylene-amine-alkylene, orcombinations of any of the foregoing groups. Preferred linking groupsinclude C₁-C₈ alkylene (e.g., ethylene or propylene), C₁-C₈ oxaalkylene,C₁-C₈ alkylene-amide-C₁-C₈ alkylene, and C₁-C₈ alkylene-amine-C₁-C₈alkylene. Particularly preferred is C₁-C₈ alkylene, especially ethylene(—CH₂CH₂—). When T in the compound of formula I is O, it is preferredthat the carbon atom of the linking group to which the O is attached behindered. For instance, if T is O and Y is alkylene, a preferredalkylene is —C(R^(H))₂(CH₂)_(x)—, where R^(H) is independently C₁-C₆alkyl (preferably independently methyl or ethyl) and x is from 1 to 5.

I-12. Compounds of formulae I, I-1, I-2, I-3, I-4, I-5, I-6, I-7, I-8,I-9, I-10, and I-11 may include compounds of formula I-12, which arecompounds of formula I, I-1, I-2, I-3, I-4, I-5, I-6, I-7, I-8, I-9,I-10, or I-11 wherein T is a bond or is NR (preferably NH).

I-13. Compounds of formulae I, I-1, I-2, I-3, I-4, I-5, I-6, I-7, I-8,I-9, I-10, I-11, and I-12 may include compounds of formula I-13, whichare compounds of formula I, I-1, I-2, I-3, I-4, I-5, I-6, I-7, I-8, I-9,I-10, I-11, or I-12 wherein EWG is cyano, amide, ester, keto, oraldehyde. Preferably, EWG is cyano.

Preferred compounds of formula I include compounds of formula II:

wherein:

-   -   m and n are independently 0, 1, 2, 3, or 4;    -   T is a bond, O, or NR;    -   X is O, S, NR, SO, or SO₂;    -   Y is a linking group;    -   P_(g) is a polymerizable group;    -   R at each occurrence is independently H, C₁-C₆ alkyl,        cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or Y—P_(g); and    -   R¹ and R², when present, are independently at each occurrence        C₁-C₆ alkyl, C₁-C₆ alkoxy, C₁-C₆ thioalkyl, C₃-C₇ cycloalkyl,        aryl (preferably unsubstituted phenyl or phenyl substituted with        alkyl or halo), halo, hydroxy, amino, NR³R⁴, or benzyl, wherein        R³ and R⁴ are independently H or C₁-C₆ alkyl, or two adjacent R¹        or R² groups, together with the carbon atoms to which they are        attached, combine to form a cycloalkyl or aryl ring. Compounds        of formula I preferably contain one or two Y—P_(g) groups. More        preferably, the compounds contain one Y—P_(g) group.

Formula II-1. Compounds of formula II may include compounds of formulaII-1, which are compounds of formula II wherein X is S.

II-2. Compounds of formula II may include compounds of formula II-2,which are compounds of formula II wherein X is O.

II-3. Compounds of formula II may include compounds of formula II-3,which are compounds of formula II wherein X is NR, preferably NH orN-alkyl.

II-4. Compounds of formula II may include compounds of formula II-4,which are compounds of formula II wherein X is SO.

II-5. Compounds of formula II may include compounds of formula II-5,which are compounds of formula II wherein X is SO₂.

II-6. Compounds of formulae II, II-1, II-2, II-3, II-4, and II-5 mayinclude compounds of formula II-6, which are compounds of formula II,II-1, II-2, II-3, II-4, or II-5 wherein m and n are independently 0 or1, or alternatively both are 0.

II-7. Compounds of formulae II, II-1, II-2, II-3, II-4, and II-5 mayinclude compounds of formula II-7, which are compounds of formula II,II-1, II-2, II-3, II-4, or II-5 wherein m is 1 and le is C₁-C₆ alkyl,preferably ethyl or methyl.

II-8. Compounds of formulae II, II-1, II-2, II-3, II-4, II-5, and II-7may include compounds of formula II-8, which are compounds of formulaII, II-1, II-2, II-3, II-4, II-5, or II-7 wherein n is 1 and R² is C₁-C₆alkyl, preferably ethyl or methyl.

II-9. Compounds of formulae II, II-1, II-2, II-3, II-4, II-5, II-6, II-7and II-8 may include compounds of formula II-9, which are compounds offormula II, II-1, II-2, II-3, II-4, II-5, II-6, II-7 or II-8 wherein Ris H, or C₁-C₆ alkyl. Preferably, R in the group T is H.

II-10. Compounds of formulae II, II-1, II-2, II-3, II-4, II-5, II-6,II-7, II-8, and II-9 may include compounds of formula II-10, which arecompounds of formula II, II-1, II-2, II-3, II-4, II-5, II-6, II-7, II-8,or II-9 wherein P_(g) (a polymerizable group) at each occurrenceindependently comprises styryl, vinyl carbonate, vinyl ether, vinylcarbamate, N-vinyl lactam, N-vinylamide, (meth)acrylate, or(meth)acrylamide. The polymerizable group allows the compounds of theinvention to form covalent bonds when reacted with monomers,crosslinking agents, and other components generally used in makingpolymeric devices. The compatibility of the compounds with the reactivemixture can be controlled via the selection of the polymerizable group(and the linking group). Preferred polymerizable groups include(meth)acrylate or (meth)acrylamide. A more preferred polymerizable groupis methacrylate.

II-11. Compounds of formulae II, II-1, II-2, II-3, II-4, II-5, II-6,II-7, II-8, II-9, and II-10 may include compounds of formula II-11,which are compounds of formula II, II-1, II-2, II-3, II-4, II-5, II-6,II-7, II-8, II-9, or II-10 wherein Y (a linking group) is alkylene,cycloalkylene, heterocycloalkylene, arylene (e.g., phenylene),heteroarylene, oxaalkylene, alkylene-amide-alkylene,alkylene-amine-alkylene, or combinations of any of the foregoing groups.Preferred linking groups include C₁-C₈ alkylene (e.g., ethylene orpropylene), C₁-C₈ oxaalkylene, C₁-C₈ alkylene-amide-C₁-C₈ alkylene, andC₁-C₈ alkylene-amine-C₁-C₈ alkylene. Particularly preferred is C₁-C₈alkylene, especially ethylene (—CH₂CH₂—). When T in the compound offormula II is O, it is preferred that the carbon atom of the linkinggroup to which the O is attached be hindered. For instance, if T is Oand Y is alkylene, a preferred alkylene is —C(R^(H))₂(CH₂)_(x)—, whereR^(H) is independently C₁-C₆ alkyl (preferably independently methyl orethyl) and x is from 1 to 5.

II-12. Compounds of formulae II, II-1, II-2, II-3, II-4, II-5, II-6,II-7, II-8, II-9, II-10, and II-11 may include compounds of formulaII-12, which are compounds of formula II, II-1, II-2, II-3, II-4, II-5,II-6, II-7, II-8, II-9, II-10, or II-11 wherein T is a bond or is NR(preferably NH).

Preferred compounds of formula I and formula II include compounds offormula III:

wherein:

-   -   m and n are independently 0, 1, 2, 3, or 4;    -   X is O, S, NR, SO, or SO₂;    -   Y is a linking group;    -   P_(g) is a polymerizable group;    -   R at each occurrence is independently H, C₁-C₆ alkyl,        cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or Y—P_(g); and    -   R¹ and R², when present, are independently at each occurrence        C₁-C₆ alkyl, C₁-C₆ alkoxy, C₁-C₆ thioalkyl, C₃-C₇ cycloalkyl,        aryl (preferably unsubstituted phenyl or phenyl substituted with        alkyl or halo), halo, hydroxy, amino, NR³R⁴, or benzyl, wherein        R³ and R⁴ are independently H or C₁-C₆ alkyl, or two adjacent R¹        or R² groups, together with the carbon atoms to which they are        attached, combine to form a cycloalkyl or aryl ring. Compounds        of formula II preferably contain one or two Y—P_(g) groups. More        preferably, the compounds contain one Y—P_(g) group.

Formula III-1. Compounds of formula III may include compounds of formulaIII-1, which are compounds of formula III wherein X is S.

III-2. Compounds of formula III may include compounds of formula III-2,which are compounds of formula III wherein X is O.

III-3. Compounds of formula III may include compounds of formula III-3,which are compounds of formula III wherein X is NR, preferably NH orN-alkyl.

III-4. Compounds of formula III may include compounds of formula III-4,which are compounds of formula III wherein X is SO.

III-5. Compounds of formula III may include compounds of formula III-5,which are compounds of formula III wherein X is SO₂.

III-6. Compounds of formulae III, III-1, III-2, III-3, III-4, and III-5may include compounds of formula III-6, which are compounds of formulaIII, III-1, III-2, III-3, III-4, or III-5 wherein m and n areindependently 0 or 1, or alternatively both are 0.

III-7. Compounds of formulae III, III-1, III-2, III-3, III-4, and III-5may include compounds of formula III-7, which are compounds of formulaIII, III-1, III-2, III-3, III-4, or III-5 wherein m is 1 and R¹ is C₁-C₆alkyl, preferably ethyl or methyl.

III-8. Compounds of formulae III, III-1, III-2, III-3, III-4, III-5, andIII-7 may include compounds of formula III-8, which are compounds offormula III, III-1, III-2, III-3, III-4, III-5, or III-7 wherein n is 1and R² is C₁-C₆ alkyl, preferably ethyl or methyl.

III-9. Compounds of formulae III, III-1, III-2, III-3, III-4, III-5,III-6, III-7 and III-8 may include compounds of formula III-9, which arecompounds of formula III, III-1, III-2, III-3, III-4, III-5, III-6,III-7 or III-8 wherein R at each occurrence is independently H, or C₁-C₆alkyl. Preferably, R at each occurrence is H. Preferably R in the groupT is H

III-10. Compounds of formulae III, III-1, III-2, III-3, III-4, III-5,III-6, III-7, III-8, and III-9 may include compounds of formula III-10,which are compounds of formula III, III-1, III-2, III-3, III-4, III-5,III-6, III-7, III-8, or III-9 wherein P_(g) (a polymerizable group) ateach occurrence independently comprises styryl, vinyl carbonate, vinylether, vinyl carbamate, N-vinyl lactam, N-vinylamide, (meth)acrylate, or(meth)acrylamide. The polymerizable group allows the compounds of theinvention to form covalent bonds when reacted with monomers,crosslinking agents, and other components generally used in makingpolymeric devices. The compatibility of the compounds with the reactivemixture can be controlled via the selection of the polymerizable group(and the linking group). Preferred polymerizable groups include(meth)acrylate or (meth)acrylamide. A more preferred polymerizable groupis methacrylate.

III-11. Compounds of formulae III, III-1, III-2, III-3, III-4, III-5,III-6, III-7, III-8, III-9, and III-10 may include compounds of formulaIII-11, which are compounds of formula III, III-1, III-2, III-3, III-4,III-5, III-6, III-7, III-8, III-9, or III-10 wherein Y (a linking group)is alkylene, cycloalkylene, heterocycloalkylene, arylene (e.g.,phenylene), heteroarylene, oxaalkylene, alkylene-amide-alkylene,alkylene-amine-alkylene, or combinations of any of the foregoing groups.Preferred linking groups include C₁-C₈ alkylene (e.g., ethylene orpropylene), C₁-C₈ oxaalkylene, C₁-C₈ alkylene-amide-C₁-C₈ alkylene, andC₁-C₈ alkylene-amine-C₁-C₈ alkylene. Particularly preferred is C₁-C₈alkylene, especially ethylene (—CH₂CH₂—).

Specific examples of compounds of formula I include, but are not limitedto, the compounds shown in Table 1.

TABLE 1

  2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl methacrylate

  2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl acrylate

  N-(2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl)methacrylamide

  N-(2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido) ethyl)acrylamide

  2-(2-cyano-N-methyl-2-(9H-thioxanthen-9-ylidene) acetamido)ethylmethacrylate

  2-cyano-2-(9H-thioxanthen-9-ylidene)-N-(2-(N-vinylacetamido)ethyl)acetamide

  2-(2-cyano-2-(9H-xanthen-9-ylidene) acetamido)ethyl methacrylate

  2-(2-cyano-2-(9H-xanthen-9-ylidene)acetamido)ethyl acrylate

  N-(2-(2-cyano-2-(9H-xanthen-9-ylidene)acetamido) ethyl)methacrylamide

  N-(2-(2-cyano-2-(9H-xanthen-9-ylidene)acetamido) ethyl)acrylamide

  2-(2-cyano-N-methyl-2-(9H-xanthen-9-ylidene)acetamido) ethylmethacrylate

  2-cyano-N-(2-(N-vinylacetamido)ethyl)-2-(9H-xanthen-9-ylidene)acetamide

  2-(2-(acridin-9(10H)-ylidene)-2-cyanoacetamido) ethyl acrylate

  N-(2-(2-(acridin-9(10H)-ylidene)-2-cyanoacetamido)ethyl)methacrylamide

  N-(2-(2-(acridin-9(10H)-ylidene)-2-cyanoacetamido) ethyl)acrylamide

  2-(2-(acridin-9(10H)-ylidene)-2-cyano-N- methylacetamido)ethylmethacrylate

  2-(acridin-9(10H)-ylidene)-2-cyano-N-(2-(N-vinylacetamido)ethyl)acetamide

  2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)-2- methylpropylmethacrylate

  2-(2-cyano-2-(9H-xanthen-9-ylidene)acetoxy)-2- methylpropyl acrylate

  (Z)-2-(2-cyano-2-(3-hydroxyacridin-9(10H)-ylidene) acetamido)ethylmethacrylate

  2-(2-cyano-2-(10-methylacridin-9(10H)-ylidene) acetamido)ethylmethacrylate

  2-(2-cyano-2-(3,6-dihydroxyacridin-9(10H)-ylidene) acetamido)ethylmethacrylate

  (E)-2-(2-(7H-benzo[c]xanthen-7-ylidene)-2- cyanoacetamido)ethylmethacrylate

  (Z)-2-(2-cyano-2-(3-methoxy-9H-xanthen-9-ylidene) acetamido)ethylmethacrylate

  2-(2-cyano-2-(3,6-dihydroxy-9H-xanthen-9-ylidene) acetamido)ethylmethacrylate

  (E)-2-(2-cyano-2-(2-methyl-9H-xanthen-9-ylidene) acetamido)ethylmethacrylate

  (E)-2-(2-cyano-2-(1-hydroxy-9H-xanthen-9-ylidene) acetamido)ethylmethacrylate

  (E)-2-(2-cyano-2-(2,4-dichloro-9H-thioxanthen-9-ylidene)acetamido)ethyl methacrylate

  (E)-2-(2-(2-chloro-9H-thioxanthen-9-ylidene)-2- cyanoacetamido)ethylmethacrylate

  (E)-2-(2-cyano-2-(2-isopropy1-9H-thioxanthen-9-ylidene)acetamido)ethyl methacrylate

  (E)-2-(2-cyano-2-(4-isopropy1-9H-thioxanthen-9-ylidene)acetamido)ethyl methacrylate

  2-(3-oxo-2-(9H-thioxanthen-9-ylidene)propanamido) ethyl methacrylate

  2-(3-oxo-2-(9H-thioxanthen-9-ylidene)butanamido) ethyl methacrylate

  2-(3-methoxy-3-oxo-2-(9H-thioxanthen-9-ylidene)propanamido) ethylmethacrylate

  2-(3-amino-3-oxo-2-(9H-thioxanthen-9-ylidene) propanamido)ethylmethacrylate

Compounds of the invention can be selected to provide targetedabsorption of UV and/or high energy visible light. Such targeting may beachieved, for example, through selection of the hetero atom of the coretricyclic structure (X in formula I). For instance, compounds of formulaI-1 (the heteroatom is sulfur) may absorb HEV light. On the other hands,compounds of formula I-2 (the heteroatom is oxygen) may absorb UV lightand some HEV light although to a lesser extent than formula I-1compounds.

Additional tuning of the absorption characteristics for a given X in thecompounds of formula I may be provided by adding or varying thesubstituents R¹ and R² to, for instance, obtain bathochromic orhypsochromic shifts. Electron donating substituents may, for example,may cause red shifts to the UV-VIS absorption spectrum, while electronwithdrawing groups may cause blue shifts; the magnitude of these shiftsmay depend on the electron donating or withdrawing ability, and theposition, of the substituent. For example, an alkoxy substituent mayresult in a smaller red shift than, for instance, an amino or thioalkylgroup at the same carbon center.

Preferred X groups in the compounds of the invention are S, O, and NR,more preferably S and O. However, additional oxidation states of sulfursuch as sulfoxide and sulfone may also provide a means to modify UV-VISspectra of the compounds. Sulfoxide and sulfone have reduced electrondensity on the sulfur atom and may be used to create hypsochromic (blue)shifted spectra.

Compounds of formula I may be used in combination with other absorbingcompounds to provide desirable absorption characteristics. For example,preferred compositions may comprise a compound of formula I-1 (X is S)and a second compound that absorbs UV. The second compound may, forexample, also be a compound of formula I that absorbs in the UV region(such as compounds of formula I-2 (X is O)), or it may be another UVabsorbing compound. Suitable UV absorbing compounds are known in theart, and fall into several classes which include, but are not limitedto, benzophenones, benzotriazoles, triazines, substitutedacrylonitriles, salicyclic acid derivatives, benzoic acid derivatives,cinnamic acid derivatives, chalcone derivatives, dypnone derivatives,crotonic acid derivatives, or any mixtures thereof. A preferred class ofUV absorbing compound is benzotriazoles, such as Norbloc(2-(2′-hydroxy-5-methacrylyloxyethylphenyl)-2H-benzotriazole).

A particularly preferred composition comprises2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl methacrylate and2-(2-cyano-2-(9H-xanthen-9-ylidene)acetamido)ethyl methacrylate. Anotherpreferred composition comprises2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl methacrylate and2-(2′-hydroxy-5-methacrylyloxyethylphenyl)-2H-benzotriazole.

Compounds of formula I may be prepared by those skilled in the art usingliterature methods. By way of example, various compounds of formula Iwhere the EWG is cyano may be prepared as shown in Scheme 1 and theassociated description. Exemplary reagents and procedures for thesereactions appear in the working examples.

Scheme 1 shows a method for preparing exemplary compounds of theinvention. Thus, the carbonyl moiety of the starting material isconverted to a reactive dihalide intermediate, which is further reactedwith the active methylene compound without further purification orisolation. The reaction mixture is protected from air and moisture untilcompletion of the reaction with the cyanomethyl amide derivative. Othercompounds of the invention may be prepared by those skilled in the artusing analogous procedures to those shown in Scheme 1 with appropriatesubstitution of reagents.

High energy light absorbing compounds, such as the compounds of formulaI, may be included in reactive mixtures to form various products,including biomedical devices and ophthalmic devices. Generally, the highenergy light absorbing compounds can be present in any amount up to thelimit of their solubility. For instance, the compounds may be present inan amount in the range of about 0.1% to about 10% by weight, or fromabout 0.5 to about 5% by weight, or from about 0.75% to about 4% byweight. The upper limit is typically determined by the solubility of thecompound with other co-monomers and or diluents in the reactive monomermix.

Preferably, the high energy light absorbing compounds of the inventionare included in ophthalmic devices. A variety of ophthalmic devices maybe prepared, including hard contact lenses, soft contact lenses, cornealonlays, corneal inlays, intraocular lenses, or overlay lenses.Preferably, the ophthalmic device is a soft contact lens, which may bemade from conventional or silicone hydrogel formulations.

Ophthalmic devices of the invention comprise a free radical reactionproduct of a reactive mixture containing one or more polymerizable highenergy light absorbing compounds, such as compounds of formula I, one ormore monomers suitable for making the desired ophthalmic device (alsoreferred to herein as device forming monomers or hydrogel formingmonomers), and optional components. Thus, the reactive mixture may, forexample, include, in addition to a polymerizable high energy lightabsorbing compound as described above, one or more of: hydrophiliccomponents, hydrophobic components, silicone-containing components,wetting agents such as polyamides, crosslinking agents, and furthercomponents such as diluents and initiators.

Hydrophilic Components

Examples of suitable families of hydrophilic monomers include(meth)acrylates, styrenes, vinyl ethers, (meth)acrylamides, N-vinyllactams, N-vinyl amides, N-vinyl imides, N-vinyl ureas, O-vinylcarbamates, O-vinyl carbonates, other hydrophilic vinyl compounds, andmixtures thereof.

Non-limiting examples of hydrophilic (meth)acrylate and (meth)acrylamidemonomers include: acrylamide, N-isopropyl acrylamide,N,N-dimethylaminopropyl (meth)acrylamide, N,N-dimethyl acrylamide (DMA),2-hydroxyethyl methacrylate (HEMA), 2-hydroxypropyl (meth)acrylate,3-hydroxypropyl (meth)acrylate, 2,3-dihydroxypropyl (meth)acrylate,2-hydroxybutyl (meth)acrylate, 3-hydroxybutyl (meth)acrylate,4-hydroxybutyl (meth)acrylate, N-(2-hydroxyethyl) (meth)acrylamide,N,N-bis(2-hydroxyethyl) (meth)acrylamide, N-(2-hydroxypropyl)(meth)acrylamide, N,N-bis(2-hydroxypropyl) (meth)acrylamide,N-(3-hydroxypropyl) (meth)acrylamide, N-(2-hydroxybutyl)(meth)acrylamide, N-(3-hydroxybutyl) (meth)acrylamide,N-(4-hydroxybutyl) (meth)acrylamide, 2-aminoethyl (meth)acrylate,3-aminopropyl (meth)acrylate, 2-aminopropyl (meth)acrylate,N-2-aminoethyl (meth)acrylamides), N-3-aminopropyl (meth)acrylamide,N-2-aminopropyl (meth)acrylamide, N,N-bis-2-aminoethyl(meth)acrylamides, N,N-bis-3-aminopropyl (meth)acrylamide),N,N-bis-2-aminopropyl (meth)acrylamide, glycerol methacrylate,polyethyleneglycol monomethacrylate, (meth)acrylic acid, vinyl acetate,acrylonitrile, and mixtures thereof.

Hydrophilic monomers may also be ionic, including anionic, cationic,zwitterions, betaines, and mixtures thereof. Non-limiting examples ofsuch charged monomers include (meth)acrylic acid,N-[(ethenyloxy)carbonyl]-β-alanine (VINAL), 3-acrylamidopropanoic acid(ACA1), 5-acrylamidopentanoic acid (ACA2), 3-acrylamido-3-methylbutanoicacid (AMBA), 2-(methacryloyloxy)ethyl trimethylammonium chloride (Q Saltor METAC), 2-acrylamido-2-methylpropane sulfonic acid (AMPS),1-propanaminium,N-(2-carboxyethyl)-N,N-dimethyl-3-[(1-oxo-2-propen-1-yl)amino]-, innersalt (CBT), 1-propanaminium,N,N-dimethyl-N-[3-[(1-oxo-2-propen-1-yl)amino]propyl]-3-sulfo-, innersalt (SBT), 3,5-Dioxa-8-aza-4-phosphaundec-10-en-1-aminium,4-hydroxy-N,N,N-trimethyl-9-oxo-, inner salt, 4-oxide (9CI) (PBT),2-methacryloyloxyethyl phosphorylcholine,3-(dimethyl(4-vinylbenzyl)ammonio)propane-1-sulfonate (DMVBAPS),3-((3-acrylamidopropyl)dimethylammonio)propane-1-sulfonate (AMPDAPS),3-((3-methacrylamidopropyl)dimethylammonio)propane-1-sulfonate(MAMPDAPS),3-((3-(acryloyloxy)propyl)dimethylammonio)propane-1-sulfonate (APDAPS),and methacryloyloxy)propyl)dimethylammonio)propane-1-sulfonate(MAPDAPS).

Non-limiting examples of hydrophilic N-vinyl lactam and N-vinyl amidemonomers include: N-vinyl pyrrolidone (NVP), N-vinyl-2-piperidone,N-vinyl-2-caprolactam, N-vinyl-3-methyl-2-caprolactam,N-vinyl-3-methyl-2-piperidone, N-vinyl-4-methyl-2-piperidone,N-vinyl-4-methyl-2-caprolactam, N-vinyl-3-ethyl-2-pyrrolidone,N-vinyl-4,5-dimethyl-2-pyrrolidone, N-vinyl acetamide (NVA),N-vinyl-N-methylacetamide (VMA), N-vinyl-N-ethyl acetamide,N-vinyl-N-ethyl formamide, N-vinyl formamide,N-vinyl-N-methylpropionamide, N-vinyl-N-methyl-2-methylpropionamide,N-vinyl-2-methylpropionamide, N-vinyl-N,N′-dimethylurea,1-methyl-3-methylene-2-pyrrolidone, 1-methyl-5-methylene-2-pyrrolidone,5-methyl-3-methylene-2-pyrrolidone; 1-ethyl-5-methylene-2-pyrrolidone,N-methyl-3-methylene-2-pyrrolidone, 5-ethyl-3-methylene-2-pyrrolidone,1-N-propyl-3-methylene-2-pyrrolidone,1-N-propyl-5-methylene-2-pyrrolidone,1-isopropyl-3-methylene-2-pyrrolidone,1-isopropyl-5-methylene-2-pyrrolidone, N-vinyl-N-ethyl acetamide,N-vinyl-N-ethyl formamide, N-vinyl formamide, N-vinyl isopropylamide,N-vinyl caprolactam, N-vinylimidazole, and mixtures thereof.

Non-limiting examples of hydrophilic O-vinyl carbamates and O-vinylcarbonates monomers include N-2-hydroxyethyl vinyl carbamate andN-carboxy-B-alanine N-vinyl ester. Further examples of hydrophilic vinylcarbonate or vinyl carbamate monomers are disclosed in U.S. Pat. No.5,070,215. Hydrophilic oxazolone monomers are disclosed in U.S. Pat. No.4,910,277.

Other hydrophilic vinyl compounds include ethylene glycol vinyl ether(EGVE), di(ethylene glycol) vinyl ether (DEGVE), allyl alcohol, and2-ethyl oxazoline.

The hydrophilic monomers may also be macromers or prepolymers of linearor branched poly(ethylene glycol), poly(propylene glycol), orstatistically random or block copolymers of ethylene oxide and propyleneoxide, having polymerizable moieties such as (meth)acrylates, styrenes,vinyl ethers, (meth)acrylamides, N-vinylamides, and the like. Themacromers of these polyethers have one polymerizable group; theprepolymers may have two or more polymerizable groups.

The preferred hydrophilic monomers of the present invention are DMA,NVP, HEMA, VMA, NVA, and mixtures thereof. Preferred hydrophilicmonomers include mixtures of DMA and HEMA. Other suitable hydrophilicmonomers will be apparent to one skilled in the art.

Generally, there are no particular restrictions with respect to theamount of the hydrophilic monomer present in the reactive monomermixture. The amount of the hydrophilic monomers may be selected basedupon the desired characteristics of the resulting hydrogel, includingwater content, clarity, wettability, protein uptake, and the like.Wettability may be measured by contact angle, and desirable contactangles are less than about 100°, less than about 80°, and less thanabout 60°. The hydrophilic monomer may be present in an amount in therange of, for instance, about 0.1 to about 100 weight percent,alternatively in the range of about 1 to about 80 weight percent,alternatively about 5 to about 65 weight percent, alternatively in therange of about 40 to about 60 weight percent, or alternatively about 55to about 60 weight percent, based on the total weight of the reactivecomponents in the reactive monomer mixture.

Silicone-Containing Components

Silicone-containing components suitable for use in the inventioncomprise one or more polymerizable compounds, where each compoundindependently comprises at least one polymerizable group, at least onesiloxane group, and one or more linking groups connecting thepolymerizable group(s) to the siloxane group(s). The silicone-containingcomponents may, for instance, contain from 1 to 220 siloxane repeatunits, such as the groups defined below. The silicone-containingcomponent may also contain at least one fluorine atom.

The silicone-containing component may comprise: one or morepolymerizable groups as defined above; one or more optionally repeatingsiloxane units; and one or more linking groups connecting thepolymerizable groups to the siloxane units. The silicone-containingcomponent may comprise: one or more polymerizable groups that areindependently a (meth)acrylate, a styryl, a vinyl ether, a(meth)acrylamide, an N-vinyl lactam, an N-vinylamide, anO-vinylcarbamate, an O-vinylcarbonate, a vinyl group, or mixtures of theforegoing; one or more optionally repeating siloxane units; and one ormore linking groups connecting the polymerizable groups to the siloxaneunits.

The silicone-containing component may comprise: one or morepolymerizable groups that are independently a (meth)acrylate, a(meth)acrylamide, an N-vinyl lactam, an N-vinylamide, a styryl, ormixtures of the foregoing; one or more optionally repeating siloxaneunits; and one or more linking groups connecting the polymerizablegroups to the siloxane units.

The silicone-containing component may comprise: one or morepolymerizable groups that are independently a (meth)acrylate, a(meth)acrylamide, or mixtures of the foregoing; one or more optionallyrepeating siloxane units; and one or more linking groups connecting thepolymerizable groups to the siloxane units.

Formula A. The silicone-containing component may comprise one or morepolymerizable compounds of Formula A:

wherein:

at least one R^(A) is a group of formula R_(g)-L- wherein R_(g) is apolymerizable group and L is a linking group, and the remaining R^(A)are each independently:

-   -   (a) R_(g)-L-,    -   (b) C₁-C₁₆ alkyl optionally substituted with one or more        hydroxy, amino, amido, oxa, carboxy, alkyl carboxy, carbonyl,        alkoxy, amido, carbamate, carbonate, halo, phenyl, benzyl, or        combinations thereof,    -   (c) C₃-C₁₂ cycloalkyl optionally substituted with one or more        alkyl, hydroxy, amino, amido, oxa, carbonyl, alkoxy, amido,        carbamate, carbonate, halo, phenyl, benzyl, or combinations        thereof,    -   (d) a C₆-C₁₄ aryl group optionally substituted with one or more        alkyl, hydroxy, amino, amido, oxa, carboxy, alkyl carboxy,        carbonyl, alkoxy, amido, carbamate, carbonate, halo, phenyl,        benzyl, or combinations thereof,    -   (e) halo,    -   (f) alkoxy, cyclic alkoxy, or aryloxy,    -   (g) siloxy,    -   (h) alkyleneoxy-alkyl or alkoxy-alkyleneoxy-alkyl, such as        polyethyleneoxyalkyl, polypropyleneoxyalkyl, or        poly(ethyleneoxy-co-propyleneoxyalkyl), or    -   (i) a monovalent siloxane chain comprising from 1 to 100        siloxane repeat units optionally substituted with alkyl, alkoxy,        hydroxy, amino, oxa, carboxy, alkyl carboxy, alkoxy, amido,        carbamate, halo or combinations thereof; and

n is from 0 to 500 or from 0 to 200, or from 0 to 100, or from 0 to 20,where it is understood that when n is other than 0, n is a distributionhaving a mode equal to a stated value. When n is 2 or more, the SiOunits may carry the same or different R^(A) substituents and ifdifferent R^(A) substituents are present, the n groups may be in randomor block configuration.

In Formula A, three R^(A) may each comprise a polymerizable group,alternatively two R^(A) may each comprise a polymerizable group, oralternatively one R^(A) may comprise a polymerizable group.

Formula B. The silicone-containing component of formula A may be amono-functional polymerizable compound of formula B:

wherein:

Rg is a polymerizable group;

L is a linking group;

j1 and j2 are each independently whole numbers from 0 to 220, providedthat the sum of j1 and j2 is from 1 to 220;

R^(A1), R^(A2), R^(A3), R^(A4), R^(A5), and R^(A7) are independently ateach occurrence C₁-C₆ alkyl, C₃-C₁₂ cycloalkyl, C₁-C₆ alkoxy, C₄-C₁₂cyclic alkoxy, alkoxy-alkyleneoxy-alkyl, aryl (e.g., phenyl), aryl-alkyl(e.g., benzyl), haloalkyl (e.g., partially or fully fluorinated alkyl),siloxy, fluoro, or combinations thereof, wherein each alkyl in theforegoing groups is optionally substituted with one or more hydroxy,amino, amido, oxa, carboxy, alkyl carboxy, carbonyl, alkoxy, carbamate,carbonate, halo, phenyl, or benzyl, each cycloalkyl is optionallysubstituted with one or more alkyl, hydroxy, amino, amido, oxa,carbonyl, alkoxy, carbamate, carbonate, halo, phenyl, or benzyl and eacharyl is optionally substituted with one or more alkyl, hydroxy, amino,amido, oxa, carboxy, alkyl carboxy, carbonyl, alkoxy, carbamate,carbonate, halo, phenyl, or benzyl; and

R^(A6) is siloxy, C₁-C₈ alkyl (e.g., C₁-C₄ alkyl, or butyl, or methyl),or aryl (e.g., phenyl), wherein alkyl and aryl may optionally besubstituted with one or more fluorine atoms.

Formula B-1. Compounds of formula B may include compounds of formulaB-1, which are compounds of formula B wherein j1 is zero and j2 is from1 to 220, or j2 is from 1 to 100, or j2 is from 1 to 50, or j2 is from 1to 20, or j2 is from 1 to 5, or j2 is 1.

B-2. Compounds of formula B may include compounds of formula B-2, whichare compounds of formula B wherein j1 and j2 are independently from 4 to100, or from 4 to 20, or from 4 to 10, or from 24 to 100, or from 10 to100.

B-3. Compounds of formulae B, B-1, and B-2 may include compounds offormula B-3, which are compounds of formula B, B-1, or B-2 whereinR^(A1), R^(A2), R^(A3), and R^(A4) are independently at each occurrenceC₁-C₆ alkyl or siloxy. Preferred alkyl are C₁-C₃ alkyl, or morepreferably, methyl. Preferred siloxy is trimethylsiloxy.

B-4. Compounds of formulae B, B-1, B-2, and B-3 may include compounds offormula B-4, which are compounds of formula B, B-1, B-2, or B-3 whereinR^(A5) and R^(A7) are independently alkoxy-alkyleneoxy-alkyl, preferablythey are independently a methoxy capped polyethyleneoxyalkyl of formulaCH₃O—[CH₂CH₂O]_(p)—CH₂CH₂CH₂, wherein p is a whole number from 1 to 50.

B-5. Compounds of formulae B, B-1, B-2, and B-3 may include compounds offormula B-5, which are compounds of formula B, B-1, B-2, or B-3 whereinR^(A5) and R^(A7) are independently siloxy, such as trimethylsiloxy.

B-6. Compounds of formulae B, B-1, B-2, and B-3 may include compounds offormula B-6, which are compounds of formula B, B-1, B-2, or B-3 whereinR^(A5) and R^(A7) are independently C₁-C₆ alkyl, alternatively C₁-C₄alkyl, or alternatively, butyl or methyl.

B-7. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, and B-6 mayinclude compounds of formula B-7, which are compounds of formula B, B-1,B-2, B-3, B-4, B-5, or B-6 wherein R^(A6) is C₁-C₈ alkyl, preferablyC₁-C₆ alkyl, more preferably C₁-C₄ alkyl (for example methyl, ethyl,n-propyl, or n-butyl). More preferably R^(A6) is n-butyl.

B-8. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, and B-7, mayinclude compounds of formula B-8, which are compounds of formula B, B-1,B-2, B-3, B-4, B-5, B-6, or B-7 wherein Rg comprises styryl, vinylcarbonate, vinyl ether, vinyl carbamate, N-vinyl lactam, N-vinylamide,(meth)acrylate, or (meth)acrylamide. Preferably, Rg comprises(meth)acrylate, (meth)acrylamide, or styryl. More preferably, Rgcomprises (meth)acrylate or (meth)acrylamide. When Rg is(meth)acrylamide, the nitrogen group may be substituted with R^(A9),wherein R^(A9) is H, C₁-C₈ alkyl (preferably C₁-C₄ alkyl, such asn-butyl, n-propyl, methyl or ethyl), or C₃-C₈ cycloalkyl (preferablyC₅-C₆ cycloalkyl), wherein alkyl and cycloalkyl are optionallysubstituted with one or more groups independently selected fromhydroxyl, amide, ether, silyl (e.g., trimethylsilyl), siloxy (e.g.,trimethylsiloxy), alkyl-siloxanyl (where alkyl is itself optionallysubstituted with fluoro), aryl-siloxanyl (where aryl is itselfoptionally substituted with fluoro), and silyl-oxaalkylene- (where theoxaalkylene is itself optionally substituted with hydroxyl).

B-9. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, and B-8may include compounds of formula B-9, which are compounds of formula B,B-1, B-2, B-3, B-4, B-5, B-6, B-7, or B-8 wherein the linking groupcomprises alkylene (preferably C₁-C₄ alkylene), cycloalkylene(preferably C₅-C₆ cycloalkylene), alkyleneoxy (preferably ethyleneoxy),haloalkyleneoxy (preferably haloethyleneoxy), amide, oxaalkylene(preferably containing 3 to 6 carbon atoms), siloxanyl,alkylenesiloxanyl, carbamate, alkyleneamine (preferably C₁-C₆alkyleneamine), or combinations of two or more thereof, wherein thelinking group is optionally substituted with one or more substituentsindependently selected from alkyl, hydroxyl, ether, amine, carbonyl,siloxy, and carbamate.

B-10. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8,and B-9 may include compounds of formula B-10, which are compounds offormula B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, or B-9 wherein thelinking group is alkylene-siloxanyl-alkylene-alkyleneoxy-, oralkylene-siloxanyl-alkylene-[alkyleneoxy-alkylene-siloxanyl]_(q)-alkyleneoxy-,where q is from 1 to 50.

B-11. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8,and B-9 may include compounds of formula B-11, which are compounds offormula B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, or B-9 wherein thelinking group is C₁-C₆ alkylene, preferably C₁-C₃ alkylene, morepreferably n-propylene.

B-12. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8,and B-9 may include compounds of formula B-12, which are compounds offormula B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, or B-9 wherein thelinking group is alkylene-carbamate-oxaalkylene. Preferably, the linkinggroup is CH₂CH₂N(H)—C(═O)—O—CH₂CH₂—O—CH₂CH₂CH₂.

B-13. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8,and B-9 may include compounds of formula B-13, which are compounds offormula B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, or B-9 wherein thelinking group is oxaalkylene. Preferably, the linking group isCH₂CH₂—O—CH₂CH₂CH₂.

B-14. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8,and B-9 may include compounds of formula B-14, which are compounds offormula B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, or B-9 wherein thelinking group is alkylene-[siloxanyl-alkylene]_(q)-, where q is from 1to 50. An example of such a linking group is:—(CH₂)₃—[Si(CH₃)₂—O—Si(CH₃)₂—(CH₂)₂]_(q)—.

B-15. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8,and B-9 may include compounds of formula B-15, which are compounds offormula B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, or B-9 wherein thelinking group isalkyleneoxy-carbamate-alkylene-cycloalkylene-carbamate-oxaalkylene,wherein cycloalkylene is optionally substituted with or 1, 2, or 3independently selected alkyl groups (preferably C₁-C₃ alkyl, morepreferably methyl). An example of such a linking group is—[OCH₂CH₂]_(q)—OC(═O)—NH—CH₂-[1,3-cyclohexylene]-NHC(═O)O—CH₂CH₂—O—CH₂CH₂—,wherein the cyclohexylene is substituted at the 1 and 5 positions with 3methyl groups.

B-16. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8,and B-9 may include compounds of formula B-16, which are compounds offormula B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, or B-9 wherein Rgcomprises styryl and the linking group is a bond or is alkyleneoxy,wherein each alkylene in alkyleneoxy is independently optionallysubstituted with hydroxyl. An example of such a linking group is—O—(CH₂)₃—. Another example of such a linking group is—O—CH₂CH(OH)CH₂—O—(CH₂)₃—.

B-17. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8,and B-9 may include compounds of formula B-17, which are compounds offormula B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, or B-9 wherein Rgcomprises styryl and the linking group is alkyleneamine. An example ofsuch a linking group is —NH—(CH₂)₃—.

B-18. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8,and B-9 may include compounds of formula B-18, which are compounds offormula B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, or B-9 wherein thelinking group is oxaalkylene optionally substituted with hydroxyl,siloxy, or silyl-alkyleneoxy (where the alkyleneoxy is itself optionallysubstituted with hydroxyl). An example of such a linking group is—CH₂CH(G)CH₂—O—(CH₂)₃—, wherein G is hydroxyl. In another example, G isR₃SiO— wherein two R groups are trimethylsiloxy and the third is C₁-C₈alkyl (preferably C₁-C₃ alkyl, more preferably methyl) or the third isC₃-C₈ cycloalkyl. In a further example, G isR₃Si—(CH₂)₃—O—CH₂CH(OH)CH₂—O—, wherein two R groups are trimethylsiloxyand the third is C₁-C₈ alkyl (preferably C₁-C₃ alkyl, more preferablymethyl) or C₃-C₈ cycloalkyl. In a still further example, G is apolymerizable group, such as (meth)acrylate. Such compounds may functionas crosslinkers.

B-19. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8,and B-9 may include compounds of formula B-19, which are compounds offormula B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, or B-9 wherein Rgcomprises styryl and the linking group is amine-oxaalkylene optionallysubstituted with hydroxyl. An example of such a linking group is—NH—CH₂CH(OH)CH₂—O—(CH₂)₃—.

B-20. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8,and B-9 may include compounds of formula B-20, which are compounds offormula B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, or B-9 wherein Rgcomprises styryl and the linking group isalkyleneoxy-carbamate-oxaalkylene. An example of such a linking group is—O—(CH₂)₂—N(H)C(═O)O—(CH₂)₂—O—(CH₂)₃—.

B-21. Compounds of formulae B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8,and B-9 may include compounds of formula B-21, which are compounds offormula B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, or B-9 wherein thelinking group is alkylene-carbamate-oxaalkylene. An example of such alinking group is —(CH₂)₂—N(H)C(═O)O—(CH₂)₂—O—(CH₂)₃—.

Formula C. Silicone-containing components of formulae A, B, B-1, B-2,B-3, B-4, B-5, B-6, B-7, B-8, B-9, B-10, B-11, B-12, B-13, B-14, B-15,B-18, and B-21 may include compounds of formula C, which are compoundsof formula A, B, B-1, B-2, B-3, B-4, B-5, B-6, B-7, B-8, B-9, B-10,B-11, B-12, B-13, B-14, B-15, B-18, or B-21 having the structure:

wherein

R^(A8) is hydrogen or methyl;

Z is O, S, or N(R^(A9)); and

L, j1, j2, R^(A1), R^(A2), R^(A3), R^(A4), R^(A5), R^(A6), R^(A7), andR^(A9) are as defined in formula B or its various sub-formulae (e.g.,B-1, B-2, etc.).

C-1. Compounds of formula C may include (meth)acrylates of formula C-1,which are compounds of formula C wherein Z is 0.

C-2. Compounds of formula C may include (meth)acrylamides of formulaC-2, which are compounds of formula C wherein Z is N(R^(A9)), and R^(A9)is H.

C-3. Compounds of formulae C may include (meth)acrylamides of formulaC-3, which are compounds of formula C wherein Z is N(R^(A9)), and R^(A9)is C₁-C₈ alkyl that is unsubstituted or is optionally substituted asindicated above. Examples of R^(A9) include CH₃, —CH₂CH(OH)CH₂(OH),—(CH₂)₃-siloxanyl, —(CH₂)₃—SiR₃, and —CH₂CH(OH)CH₂—O—(CH₂)₃—SiR₃ whereeach R in the foregoing groups is independently selected fromtrimethylsiloxy, C₁-C₈ alkyl (preferably C₁-C₃ alkyl, more preferablymethyl), and C₃-C₈ cycloalkyl. Further examples of R^(A9) include:—(CH₂)₃—Si(Me)(SiMe₃)₂, and —(CH₂)₃—Si(Me₂)-[O—SiMe₂]₁₋₁₀-CH₃.

Formula D. Compounds of formula C may include compounds of formula D:

wherein

R^(A8) is hydrogen or methyl;

Z¹ is O or N(R^(A9));

L¹ is alkylene containing 1 to 8 carbon atoms, or oxaalkylene containing3 to 10 carbon atoms, wherein L¹ is optionally substituted withhydroxyl; and

j2, R^(A3), R^(A4), R^(A5), R^(A6), R^(A7), and R^(A9) are as definedabove in formula B or its various sub-formulae (e.g., B-1, B-2, etc.).

D-1. Compounds of formula D may include compounds of formula D-1, whichare compounds of formula D wherein L¹ is C₂-C₅ alkylene optionallysubstituted with hydroxyl. Preferably L¹ is n-propylene optionallysubstituted with hydroxyl.

D-2. Compounds of formula D may include compounds of formula D-2, whichare compounds of formula D wherein L¹ is oxaalkylene containing 4 to 8carbon atoms optionally substituted with hydroxyl. Preferably L¹ isoxaalkylene containing five or six carbon atoms optionally substitutedwith hydroxyl. Examples include —(CH₂)₂—O—(CH₂)₃—, and—CH₂CH(OH)CH₂—O—(CH₂)₃—.

D-3. Compounds of formulae D, D-1, and D-2 may include compounds offormula D-3, which are compounds of formula D, D-1, or D-2 wherein Z¹ isO.

D-4. Compounds of formulae D, D-1, and D-2 may include compounds offormula D-4, which are compounds of formula D, D-1, or D-2 wherein Z¹ isN(R^(A9)), and R^(A9) is H.

D-5. Compounds of formulae D, D-1, and D-2 may include compounds offormula D-5, which are compounds of formula D, D-1, or D-2 wherein Z¹ isN(R^(A9)), and R^(A9) is C₁-C₄ alkyl optionally substituted with 1 or 2substituents selected from hydroxyl, siloxy, and C₁-C₆ alkyl-siloxanyl-.

D-6. Compounds of formulae D, D-1, D-2, D-3, D-4, and D-5 may includecompounds of formula D-6, which are compounds of formula D, D-1, D-2,D-3, D-4, or D-5 wherein j2 is 1.

D-7. Compounds of formulae D, D-1, D-2, D-3, D-4, and D-5 may includecompounds of formula D-7, which are compounds of formula D, D-1, D-2,D-3, D-4, or D-5 wherein j2 is from 2 to 220, or from 2 to 100, or from10 to 100, or from 24 to 100, or from 4 to 20, or from 4 to 10.

D-8. Compounds of formulae D, D-1, D-2, D-3, D-4, D-5, D-6, and D-7 mayinclude compounds of formula D-8, which are compounds of formula D, D-1,D-2, D-3, D-4, D-5, D-6, or D-7 wherein R^(A3), R^(A4), R^(A5), R^(A6),and R^(A7) are independently C₁-C₆ alkyl or siloxy. Preferably R^(A3),R^(A4), R^(A5), R^(A6), and R^(A7) are independently selected frommethyl, ethyl, n-propyl, n-butyl, and trimethylsiloxy. More preferably,R^(A3), R^(A4), R^(A5), R^(A6), and R^(A7) are independently selectedfrom methyl, n-butyl, and trimethylsiloxy.

D-9. Compounds of formulae D, D-1, D-2, D-3, D-4, D-5, D-6, and D-7 mayinclude compounds of formula D-9, which are compounds of formula D, D-1,D-2, D-3, D-4, D-5, D-6, or D-7 wherein R^(A3) and R^(A4) areindependently C₁-C₆ alkyl (e.g., methyl or ethyl) or siloxy (e.g.,trimethylsiloxy), and R^(A5), R^(A6), and R^(A7) are independently C₁-C₆alkyl (e.g., methyl, ethyl, n-propyl, or n-butyl).

Formula E. The silicone-containing component for use in the inventionmay comprise a multi-functional silicone-containing component. Thus, forexample, the silicone-containing component of formula A may comprise abifunctional material of formula E:

wherein

Rg, L, j1, j2, R^(A1), R^(A2), R^(A3), R^(A4), R^(A5), and R^(A7) are asdefined above for formula B or its various sub-formulae (e.g., B-1, B-2,etc.);

L² is a linking group; and

Rg¹ is a polymerizable group.

E-1. Compounds of formula E may include compounds of formula E-1, whichare compounds of formula E wherein Rg and Rg^(l) are each a vinylcarbonate of structure CH₂═CH—O—C(═O)—O— or structureCH₂═C(CH₃)—O—C(═O)—O—.

E-2. Compounds of formula E may include compounds of formula E-2, whichare compounds of formula E wherein Rg and Rg¹ are each (meth)acrylate.

E-3. Compounds of formula E may include compounds of formula E-3, whichare compounds of formula E wherein Rg and Rg¹ are each (meth)acrylamide,wherein the nitrogen group may be substituted with R^(A9) (whereinR^(A9) is as defined above).

E-4. Suitable compounds of formulae E, E-1, E-2, and E-3 includecompounds of formula E-4, which are compounds of formula E, E-1, E-2, orE-3 wherein j1 is zero and j2 is from 1 to 220, or j2 is from 1 to 100,or j2 is from 1 to 50, or j2 is from 1 to 20.

E-5. Suitable compounds of formulae E, E-1, E-2, and E-3 includecompounds of formula E-5, which are compounds of formula E, E-1, E-2, orE-3, wherein j1 and j2 are independently from 4 to 100.

E-6. Suitable compounds of formulae E, E-1, E-2, E-3, E-4, and E-5include compounds of formula E-6, which are compounds of formula E, E-1,E-2, E-3, E-4, or E-5 wherein R^(A1), R^(A2), R^(A3), R^(A4), and R^(A5)are independently at each occurrence C₁-C₆ alkyl, preferably they areindependently C₁-C₃ alkyl, or preferably, each is methyl.

E-7. Suitable compounds of formulae E, E-1, E-2, E-3, E-4, E-5, and E-6include compounds of formula E-7, which are compounds of formula E, E-1,E-2, E-3, E-4, E-5, or E-6 wherein R^(A7) is alkoxy-alkyleneoxy-alkyl,preferably it is a methoxy capped polyethyleneoxyalkyl of formulaCH₃O—[CH₂CH₂O]_(p)—CH₂CH₂CH₂, wherein p is a whole number from 1 to 50,or from 1 to 30, or from 1 to 10, or from 6 to 10.

E-8. Suitable compounds of formulae E, E-1, E-2, E-3, E-4, E-5, E-6, andE-7 include compounds of formula E-8, which are compounds of formula E,E-1, E-2, E-3, E-4, E-5, E-6, or E-7 wherein L comprises alkylene,carbamate, siloxanyl, cycloalkylene, amide, haloalkyleneoxy,oxaalkylene, or combinations of two or more thereof, wherein the linkinggroup is optionally substituted with one or more substituentsindependently selected from alkyl, hydroxyl, ether, amine, carbonyl, andcarbamate.

E-9. Suitable compounds of formulae E, E-1, E-2, E-3, E-4, E-5, E-6,E-7, and E-8 include compounds of formula E-9, which are compounds offormula E, E-1, E-2, E-3, E-4, E-5, E-6, E-7, or E-8 wherein L²comprises alkylene, carbamate, siloxanyl, cycloalkylene, amide,haloalkyleneoxy, oxaalkylene, or combinations of two or more thereof,wherein the linking group is optionally substituted with one or moresubstituents independently selected from alkyl, hydroxyl, ether, amine,carbonyl, and carbamate.

Examples of silicone-containing components suitable for use in theinvention include, but are not limited to, compounds listed in Table 2.Where the compounds in Table 2 contain polysiloxane groups, the numberof SiO repeat units in such compounds, unless otherwise indicated, ispreferably from 3 to 100, more preferably from 3 to 40, or still morepreferably from 3 to 20.

TABLE 2  1 mono-methacryloxypropyl terminated mono-n-butyl terminatedpolydimethylsiloxanes (mPDMS) (preferably containing from 3 to 15 SiOrepeating units)  2 mono-acryloxypropyl terminated mono-n-butylterminated polydimethylsiloxane  3 mono(meth)acryloxypropyl terminatedmono-n-methyl terminated polydimethylsiloxane  4mono(meth)acryloxypropyl terminated mono-n-butyl terminatedpolydiethylsiloxane  5 mono(meth)acryloxypropyl terminated mono-n-methylterminated polydiethylsiloxane  6mono(meth)acrylamidoalkylpolydialkylsiloxanes  7 mono(meth)acryloxyalkylterminated mono-alkyl polydiarylsiloxanes  83-methacryloxypropyltris(trimethylsiloxy)silane (TRIS)  93-methacryloxypropylbis(trimethylsiloxy)methylsilane 103-methacryloxypropylpentamethyl disiloxane 11mono(meth)acrylamidoalkylpolydialkylsiloxanes 12mono(meth)acrylamidoalkyl polydimethylsiloxanes 13N-(2,3-dihydroxypropane)-N′-(propyltetra(dimethylsiloxy)dimethylbutylsilane)acrylamide14 N-[3-tris(trimethylsiloxy)silyl]-propyl acrylamide (TRIS-Am) 152-hydroxy-3-[3-methy1-3,3-di(trimethylsiloxy)silylpropoxy]-propylmethacrylate (SiMAA) 162-hydroxy-3-methacryloxypropyloxypropyl-tris(trimethylsiloxy)silane 17

18

19

20

21

22

23

24

Additional non-limiting examples of suitable silicone-containingcomponents are listed in Table 3. Unless otherwise indicated, j2 whereapplicable is preferably from 1 to 100, more preferably from 3 to 40, orstill more preferably from 3 to 15. In compounds containing j1 and j2,the sum of j1 and j2 is preferably from 2 to 100, more preferably from 3to 40, or still more preferably from 3 to 15.

TABLE 3 25

26

27

28

29

30 1,3-bis[4-(vinyloxycarbonyloxy)but-1-yl]tetramethyl-disiloxane 313-(vinyloxycarbonylthio) propyl-[tris (trimethylsiloxy)silane] 323-[tris(trimethylsiloxy)silyl] propyl allyl carbamate 333-[tris(trimethylsiloxy)silyl] propyl vinyl carbamate 34tris(trimethylsiloxy)silylstyrene (Styryl-TRIS) 35

36

37

38

39

40

41

Mixtures of silicone-containing components may be used. By way ofexample, suitable mixtures may include, but are not limited to: amixture of mono-(2-hydroxy-3-methacryloxypropyloxy)-propyl terminatedmono-n-butyl terminated polydimethylsiloxane (OH-mPDMS) having differentmolecular weights, such as a mixture of OH-mPDMS containing 4 and 15 SiOrepeat units; a mixture of OH-mPDMS with different molecular weights(e.g., containing 4 and 15 repeat SiO repeat units) together with asilicone based crosslinker, such asbis-3-acryloxy-2-hydroxypropyloxypropyl polydimethylsiloxane (ac-PDMS);a mixture of2-hydroxy-3-[3-methyl-3,3-di(trimethylsiloxy)silylpropoxy]-propylmethacrylate (SiMAA) and mono-methacryloxypropyl terminated mono-n-butylterminated polydimethylsiloxane (mPDMS), such as mPDMS 1000.

Silicone-containing components for use in the invention may have anaverage molecular weight of from about 400 to about 4000 daltons.

The silicone containing component(s) may be present in amounts up toabout 95 weight %, or from about 10 to about 80 weight %, or from about20 to about 70 weight %, based upon all reactive components of thereactive mixture (excluding diluents).

Polyamides

The reactive mixture may include at least one polyamide. As used herein,the term “polyamide” refers to polymers and copolymers comprisingrepeating units containing amide groups. The polyamide may comprisecyclic amide groups, acyclic amide groups and combinations thereof andmay be any polyamide known to those of skill in the art. Acyclicpolyamides comprise pendant acyclic amide groups and are capable ofassociation with hydroxyl groups. Cyclic polyamides comprise cyclicamide groups and are capable of association with hydroxyl groups.

Examples of suitable acyclic polyamides include polymers and copolymerscomprising repeating units of Formulae G1 and G2:

wherein X is a direct bond, —(CO)—, or —(CONHR₄₄)—, wherein R₄₄ is a C₁to C₃ alkyl group; R₄₀ is selected from H, straight or branched,substituted or unsubstituted C₁ to C₄ alkyl groups; R₄₁ is selected fromH, straight or branched, substituted or unsubstituted C₁ to C₄ alkylgroups, amino groups having up to two carbon atoms, amide groups havingup to four carbon atoms, and alkoxy groups having up to two carbongroups; R₄₂ is selected from H, straight or branched, substituted orunsubstituted C₁ to C₄ alkyl groups; or methyl, ethoxy, hydroxyethyl,and hydroxymethyl; R₄₃ is selected from H, straight or branched,substituted or unsubstituted C₁ to C₄ alkyl groups; or methyl, ethoxy,hydroxyethyl, and hydroxymethyl; wherein the number of carbon atoms inR₄₀ and R₄₁ taken together is 8 or less, including 7, 6, 5, 4, 3, orless; and wherein the number of carbon atoms in R₄₂ and R₄₃ takentogether is 8 or less, including 7, 6, 5, 4, 3, or less. The number ofcarbon atoms in R₄₀ and R₄₁ taken together may be 6 or less or 4 orless. The number of carbon atoms in R₄₂ and R₄₃ taken together may be 6or less. As used herein substituted alkyl groups include alkyl groupssubstituted with an amine, amide, ether, hydroxyl, carbonyl or carboxygroups or combinations thereof.

R₄₀ and R₄₁ may be independently selected from H, substituted orunsubstituted C₁ to C₂ alkyl groups. X may be a direct bond, and R₄₀ andR₄₁ may be independently selected from H, substituted or unsubstitutedC₁ to C₂ alkyl groups. R₄₂ and R₄₃ can be independently selected from H,substituted or unsubstituted C₁ to C₂ alkyl groups, methyl, ethoxy,hydroxyethyl, and hydroxymethyl.

The acyclic polyamides of the present invention may comprise a majorityof the repeating units of Formula LV or Formula LVI, or the acyclicpolyamides can comprise at least 50 mole percent of the repeating unitof Formula G or Formula G1, including at least 70 mole percent, and atleast 80 mole percent. Specific examples of repeating units of Formula Gand Formula G1 include repeating units derived fromN-vinyl-N-methylacetamide, N-vinylacetamide,N-vinyl-N-methylpropionamide, N-vinyl-N-methyl-2-methylpropionamide,N-vinyl-2-methyl-propionamide, N-vinyl-N,N′-dimethylurea, N,N-dimethylacrylamide, methacrylamide, and acyclic amides of Formulae G2and G3:

Examples of suitable cyclic amides that can be used to form the cyclicpolyamides of include α-lactam, β-lactam, γ-lactam, δ-lactam, andε-lactam. Examples of suitable cyclic polyamides include polymers andcopolymers comprising repeating units of Formula G4:

wherein R₄₅ is a hydrogen atom or methyl group; wherein f is a numberfrom 1 to 10; wherein X is a direct bond, —(CO)—, or —(CONHR₄₆)—,wherein R₄₆ is a C₁ to C₃ alkyl group. In Formula LIX, f may be 8 orless, including 7, 6, 5, 4, 3, 2, or 1. In Formula G4, f may be 6 orless, including 5, 4, 3, 2, or 1. In Formula G4, f may be from 2 to 8,including 2, 3, 4, 5, 6, 7, or 8. In Formula LIX, f may be 2 or 3. WhenX is a direct bond, f may be 2. In such instances, the cyclic polyamidemay be polyvinylpyrrolidone (PVP).

The cyclic polyamides of the present invention may comprise 50 molepercent or more of the repeating unit of Formula G4, or the cyclicpolyamides can comprise at least 50 mole percent of the repeating unitof Formula G4, including at least 70 mole percent, and at least 80 molepercent.

The polyamides may also be copolymers comprising repeating units of bothcyclic and acyclic amides. Additional repeating units may be formed frommonomers selected from hydroxyalkyl(meth)acrylates,alkyl(meth)acrylates, other hydrophilic monomers and siloxanesubstituted (meth)acrylates. Any of the monomers listed as suitablehydrophilic monomers may be used as co-monomers to form the additionalrepeating units. Specific examples of additional monomers which may beused to form polyamides include 2-hydroxyethyl (meth)acrylate, vinylacetate, acrylonitrile, hydroxypropyl (meth)acrylate, methyl(meth)acrylate and hydroxybutyl (meth)acrylate, dihydroxypropyl(meth)acrylate, polyethylene glycol mono(meth)acrylate, and the like andmixtures thereof. Ionic monomers may also be included. Examples of ionicmonomers include (meth)acrylic acid, N-[(ethenyloxy)carbonyl]-β-alanine(VINAL, CAS #148969-96-4), 3-acrylamidopropanoic acid (ACA1),5-acrylamidopentanoic acid (ACA2), 3-acrylamido-3-methylbutanoic acid(AMBA), 2-(methacryloyloxy)ethyl trimethylammonium chloride (Q Salt orMETAC), 2-acrylamido-2-methylpropane sulfonic acid (AMPS),1-propanaminium,N-(2-carboxyethyl)-N,N-dimethyl-3-[(1-oxo-2-propen-1-yl)amino]-, innersalt (CBT, carboxybetaine; CAS 79704-35-1), 1-propanaminium,N,N-dimethyl-N-[3-[(1-oxo-2-propen-1-yl)amino]propyl]-3-sulfo-, innersalt (SBT, sulfobetaine, CAS 80293-60-3),3,5-Dioxa-8-aza-4-phosphaundec-10-en-1-aminium,4-hydroxy-N,N,N-trimethyl-9-oxo-, inner salt, 4-oxide (9CI) (PBT,phosphobetaine, CAS 163674-35-9, 2-methacryloyloxyethylphosphorylcholine, 3-(dimethyl(4-vinylbenzyl)ammonio)propane-1-sulfonate(DMVBAPS), 3-((3-acrylamidopropyl)dimethylammonio)propane-1-sulfonate(AMPDAPS),3-((3-methacrylamidopropyl)dimethylammonio)propane-1-sulfonate(MAMPDAPS),3-((3-(acryloyloxy)propyl)dimethylammonio)propane-1-sulfonate (APDAPS),methacryloyloxy)propyl)dimethylammonio)propane-1-sulfonate (MAPDAPS).

The reactive monomer mixture may comprise both an acyclic polyamide anda cyclic polyamide or copolymers thereof. The acyclic polyamide can beany of those acyclic polyamides described herein or copolymers thereof,and the cyclic polyamide can be any of those cyclic polyamides describedherein or copolymers thereof. The polyamide may be selected from thegroup polyvinylpyrrolidone (PVP), polyvinylmethyacetamide (PVMA),polydimethylacrylamide (PDMA), polyvinylacetamide (PNVA),poly(hydroxyethyl(meth)acrylamide), polyacrylamide, and copolymers andmixtures thereof. The polyamide may be a mixture of PVP (e.g., PVP K90)and PVMA (e.g., having a Mw of about 570 KDa).

The total amount of all polyamides in the reactive mixture may be in therange of between 1 weight percent and about 35 weight percent, includingin the range of about 1 weight percent to about 15 weight percent, andin the range of about 5 weight percent to about 15 weight percent, inall cases, based on the total weight of the reactive components of thereactive monomer mixture.

Without intending to be bound by theory, when used with a siliconehydrogel, the polyamide functions as an internal wetting agent. Thepolyamides of the present invention may be non-polymerizable, and inthis case, are incorporated into the silicone hydrogels assemi-interpenetrating networks. The polyamides are entrapped orphysically retained within the silicone hydrogels. Alternatively, thepolyamides of the present invention may be polymerizable, for example aspolyamide macromers or prepolymers, and in this case, are covalentlyincorporated into the silicone hydrogels. Mixtures of polymerizable andnon-polymerizable polyamides may also be used.

When the polyamides are incorporated into the reactive monomer mixturethey may have a weight average molecular weight of at least 100,000daltons; greater than about 150,000; between about 150,000 to about2,000,000 daltons; between about 300,000 to about 1,800,000 daltons.Higher molecular weight polyamides may be used if they are compatiblewith the reactive monomer mixture.

Cross-Linking Agents

It is generally desirable to add one or more cross-linking agents, alsoreferred to as cross-linking monomers, multi-functional macromers, andprepolymers, to the reactive mixture. The cross-linking agents may beselected from bifunctional crosslinkers, trifunctional crosslinkers,tetrafunctional crosslinkers, and mixtures thereof, includingsilicone-containing and non-silicone containing cross-linking agents.Non-silicone-containing cross-linking agents include ethylene glycoldimethacrylate (EGDMA), tetraethylene glycol dimethacrylate (TEGDMA),trimethylolpropane trimethacrylate (TMPTMA), triallyl cyanurate (TAC),glycerol trimethacrylate, methacryloxyethyl vinylcarbonate (HEMAVc),allylmethacrylate, methylene bisacrylamide (MBA), and polyethyleneglycol dimethacrylate wherein the polyethylene glycol has a molecularweight up to about 5000 Daltons. The cross-linking agents are used inthe usual amounts, e.g., from about 0.000415 to about 0.0156 mole per100 grams of reactive Formulas in the reactive mixture. Alternatively,if the hydrophilic monomers and/or the silicone-containing componentsare multifunctional by molecular design or because of impurities, theaddition of a cross-linking agent to the reactive mixture is optional.Examples of hydrophilic monomers and macromers which can act as thecross-linking agents and when present do not require the addition of anadditional cross-linking agent to the reactive mixture include(meth)acrylate and (meth)acrylamide endcapped polyethers. Othercross-linking agents will be known to one skilled in the art and may beused to make the silicone hydrogel of the present invention.

It may be desirable to select crosslinking agents with similarreactivity to one or more of the other reactive components in theformulation. In some cases, it may be desirable to select a mixture ofcrosslinking agents with different reactivity in order to control somephysical, mechanical or biological property of the resulting siliconehydrogel. The structure and morphology of the silicone hydrogel may alsobe influenced by the diluent(s) and cure conditions used.

Multifunctional silicone-containing components, including macromers,cross-linking agents, and prepolymers, may also be included to furtherincrease the modulus and retain tensile strength. The siliconecontaining cross-linking agents may be used alone or in combination withother cross-linking agents. An example of a silicone containingcomponent which can act as a cross-linking agent and, when present, doesnot require the addition of a crosslinking monomer to the reactivemixture includes α, ω-bismethacryloxypropyl polydimethylsiloxane.Another example is bis-3-acryloxy-2-hydroxypropyloxypropylpolydimethylsiloxane (ac-PDMS).

Cross-linking agents that have rigid chemical structures andpolymerizable groups that undergo free radical polymerization may alsobe used. Non-limiting examples of suitable rigid structures includecross-linking agents comprising phenyl and benzyl ring, such are1,4-phenylene diacrylate, 1,4-phenylene dimethacrylate,2,2-bis(4-methacryloxyphenyl)-propane,2,2-bis[4-(2-acryloxyethoxy)phenyl]propane,2,2-bis[4-(2-hydroxy-3-methacryloxypropoxy)-phenyl]propane, and4-vinylbenzyl methacrylate, and combinations thereof. Rigid crosslinkingagents may be included in amounts between about 0.5 and about 15, or2-10, 3-7 based upon the total weight of all of the reactive components.The physical and mechanical properties of the silicone hydrogels of thepresent invention may be optimized for a particular use by adjusting thecomponents in the reactive mixture.

Non-limiting examples of silicone cross-linking agents also include themulti-functional silicone-containing components described above, such ascompounds of Formula E (and its sub-formulae) and the multi-functionalcompounds shown in Table 3.

Further Constituents

The reactive mixture may contain additional components such as, but notlimited to, diluents, initiators, UV absorbers, visible light absorbers,photochromic compounds, pharmaceuticals, nutraceuticals, antimicrobialsubstances, tints, pigments, copolymerizable dyes, nonpolymerizabledyes, release agents, and combinations thereof.

Classes of suitable diluents for silicone hydrogel reactive mixturesinclude alcohols having 2 to 20 carbon atoms, amides having 10 to 20carbon atoms derived from primary amines and carboxylic acids having 8to 20 carbon atoms. The diluents may be primary, secondary, and tertiaryalcohols.

Generally, the reactive components are mixed in a diluent to form areactive mixture. Suitable diluents are known in the art. For siliconehydrogels, suitable diluents are disclosed in WO 03/022321 and U.S. Pat.No. 6,020,445, the disclosure of which is incorporated herein byreference. Classes of suitable diluents for silicone hydrogel reactivemixtures include alcohols having 2 to 20 carbons, amides having 10 to 20carbon atoms derived from primary amines, and carboxylic acids having 8to 20 carbon atoms. Primary and tertiary alcohols may be used. Preferredclasses include alcohols having 5 to 20 carbons and carboxylic acidshaving 10 to 20 carbon atoms. Specific diluents which may be usedinclude 1-ethoxy-2-propanol, diisopropylaminoethanol, isopropanol,3,7-dimethyl-3-octanol, 1-decanol, 1-dodecanol, 1-octanol, 1-pentanol,2-pentanol, 1-hexanol, 2-hexanol, 2-octanol, 3-methyl-3-pentanol,tert-amyl alcohol, tert-butanol, 2-butanol, 1-butanol,2-methyl-2-pentanol, 2-propanol, 1-propanol, ethanol, 2-ethyl-1-butanol,(3-acetoxy-2-hydroxypropyloxy)-propylbis(trimethylsiloxy) methyl silane,1-tert-butoxy-2-propanol, 3,3-dimethyl-2-butanol, tert-butoxyethanol,2-octyl-1-dodecanol, decanoic acid, octanoic acid, dodecanoic acid,2-(diisopropylamino)ethanol mixtures thereof and the like. Examples ofamide diluents include N,N-dimethyl propionamide and dimethyl acetamide.

Preferred diluents include 3,7-dimethyl-3-octanol, 1-dodecanol,1-decanol, 1-octanol, 1-pentanol, 1-hexanol, 2-hexanol, 2-octanol,3-methyl-3-pentanol, 2-pentanol, t-amyl alcohol, tert-butanol,2-butanol, 1-butanol, 2-methyl-2-pentanol, 2-ethyl-1-butanol, ethanol,3,3-dimethyl-2-butanol, 2-octyl-1-dodecanol, decanoic acid, octanoicacid, dodecanoic acid, mixtures thereof and the like.

More preferred diluents include 3,7-dimethyl-3-octanol, 1-dodecanol,1-decanol, 1-octanol, 1-pentanol, 1-hexanol, 2-hexanol, 2-octanol,1-dodecanol, 3-methyl-3-pentanol, 1-pentanol, 2-pentanol, t-amylalcohol, tert-butanol, 2-butanol, 1-butanol, 2-methyl-2-pentanol,2-ethyl-1-butanol, 3,3-dimethyl-2-butanol, 2-octyl-1-dodecanol, mixturesthereof and the like. If a diluent is present, generally there are noparticular restrictions with respect to the amount of diluent present.When diluent is used, the diluent may be present in an amount in therange of about 2 to about 70 weight percent, including in the range ofabout 5 to about 50 weight percent, and in the range of about 15 toabout 40 weight percent, based on the total weight of the reactivemixtures (including reactive and nonreactive Formulas). Mixtures ofdiluents may be used.

A polymerization initiator may be used in the reactive mixture. Thepolymerization initiator may include, for instance, at least one oflauroyl peroxide, benzoyl peroxide, iso-propyl percarbonate,azobisisobutyronitrile, and the like, that generate free radicals atmoderately elevated temperatures, and photoinitiator systems such asaromatic alpha-hydroxy ketones, alkoxyoxybenzoins, acetophenones,acylphosphine oxides, bisacylphosphine oxides, and a tertiary amine plusa diketone, mixtures thereof and the like. Illustrative examples ofphotoinitiators are 1-hydroxycyclohexyl phenyl ketone,2-hydroxy-2-methyl-1-phenyl-propan-1-one,bis(2,6-dimethoxybenzoyl)-2,4-4-trimethylpentyl phosphine oxide(DMBAPO), bis(2,4,6-trimethylbenzoyl)-phenyl phosphine eoxide (Irgacure819), 2,4,6-trimethylbenzyldiphenyl phos-phine oxide and2,4,6-trimethylbenzoyl diphenylphosphine oxide, benzoin methyl ester anda combination of cam-phorquinone and ethyl4-(N,N-dimethylamino)benzoate.

Commercially available (from IGM Resins B.V., The Netherlands) visiblelight initiator systems include Irgacure® 819, Irgacure® 1700, Irgacure®1800, Irgacure® 819, Irgacure® 1850 and Lucrin® TPO initiator.Commercially available (from IGM Resins B.V.) UV photoinitiators includeDarocur® 1173 and Darocur® 2959. These and other photoinitiators whichmay be used are disclosed in Volume III, Photoinitiators for FreeRadical Cationic & Anionic Photopolymerization, 2nd Edition by J. V.Crivello & K. Dietliker; edited by G. Bradley; John Wiley and Sons; NewYork; 1998. The initiator is used in the reactive mixture in effectiveamounts to initiate photopolymerization of the reactive mixture, e.g.,from about 0.1 to about 2 parts by weight per 100 parts of reactivemonomer mixture. Polymerization of the reactive mixture can be initiatedusing the appropriate choice of heat or visible or ultraviolet light orother means depending on the polymerization initiator used.Alternatively, initiation can be conducted using e-beam without aphotoinitiator. However, when a photoinitiator is used, the preferredinitiators are bisacylphosphine oxides, such asbis(2,4,6-tri-methylbenzoyl)-phenyl phosphine oxide (Irgacure® 819) or acombination of 1-hydroxycyclohexyl phenyl ketone andbis(2,6-dimethoxybenzoyl)-2,4-4-trimethylpentyl phosphine oxide(DMBAPO).

The reactive mixture for making the ophthalmic devices of the inventionmay comprise, in addition to a high energy light absorbing compound, anyof the polymerizable compounds and optional components described above.

Preferred reactive mixtures may comprise: a high energy light absorbingcompound, such as a formula I compound, and a hydrophilic component.

Preferred reactive mixtures may comprise: a high energy light absorbingcompound, such as a formula I compound, and a hydrophilic componentselected from DMA, NVP, HEMA, VMA, NVA, methacrylic acid, and mixturesthereof. Preferred are mixtures of HEMA and methacrylic acid.

Preferred reactive mixtures may comprise: a high energy light absorbingcompound, such as a formula I compound, a hydrophilic component, and asilicone-containing component.

Preferred reactive mixtures may comprise: a high energy light absorbingcompound, such as a formula I compound, a hydrophilic component, and asilicone-containing component comprising a compound of formula D (or itssub-formulae, such as D-1, D-2, etc.).

Preferred reactive mixtures may comprise: a high energy light absorbingcompound, such as a formula I compound, a hydrophilic component selectedfrom DMA, NVP, HEMA, VMA, NVA, and mixtures thereof; asilicone-containing component comprising a compound of formula D (or itssub-formulae, such as D-1, D-2, etc.); and an internal wetting agent.

Preferred reactive mixtures may comprise: a high energy light absorbingcompound, such as a formula I compound, a hydrophilic component selectedfrom DMA, HEMA and mixtures thereof; a silicone-containing componentselected from2-hydroxy-3-[3-methyl-3,3-di(trimethylsiloxy)silylpropoxy]-propylmethacrylate (SiMAA), mono-methacryloxypropyl terminated mono-n-butylterminated polydimethylsiloxane (mPDMS),mono-(2-hydroxy-3-methacryloxypropyl)-propyl ether terminatedmono-n-butyl terminated polydimethylsiloxane (OH-mPDMS), and mixturesthereof; and a wetting agent (preferably PVP or PVMA). For thehydrophilic component, mixtures of DMA and HEMA are preferred. For thesilicone containing component, mixtures of SiMAA and mPDMS arepreferred.

Preferred reactive mixtures may comprise: a high energy light absorbingcompound, such as a formula I compound, a hydrophilic componentcomprising a mixture of DMA and HEMA; a silicone-containing componentcomprising a mixture of OH-mPDMS having from 2 to 20 repeat units(preferably a mixture of 4 and 15 repeat units). Preferably, thereactive mixture further comprises a silicone-containing crosslinker,such as ac-PDMS. Also preferably, the reactive mixture contains awetting agent (preferably DMA, PVP, PVMA or mixtures thereof).

Preferred reactive mixtures may comprise: a high energy light absorbingcompound, such as a formula I compound; between about 1 and about 15 wt% at least one polyamide (e.g., an acyclic polyamide, a cyclicpolyamide, or mixtures thereof); at least one first mono-functional,hydroxyl substituted poly(disubstituted siloxane) having 4 to 8 siloxanerepeating units (e.g, OH-mPDMS where n is 4 to 8, preferably n is 4); atleast one second hydroxyl substituted poly(disubstituted siloxane) thatis a mono-functional hydroxyl substituted poly(disubstituted siloxane)shaving 10 to 200 or 10-100 or 10-50 or 10-20 siloxane repeating units(e.g., OH-mPDMS where n is 10 to 200 or 10-100 or 10-50 or 10-20,preferably n is 15); about 5 to about 35 wt % of at least onehydrophilic monomer; and optionally a multifunctional hydroxylsubstituted poly(disubstituted siloxane)s having 10 to 200, or 10 to 100siloxane repeating units (e.g., ac-PDMS). Preferably, the firstmono-functional, hydroxyl substituted poly(disubstituted siloxane) andthe second hydroxyl substituted poly(disubstituted siloxane) are presentin concentrations to provide a ratio of weight percent of the firstmono-functional, hydroxyl substituted poly(disubstituted siloxane) toweight percent of the second hydroxyl substituted poly(disubstitutedsiloxane) of 0.4-1.3, or 0.4-1.0.

The foregoing reactive mixtures may contain optional ingredients suchas, but not limited to, one or more initiators, internal wetting agents,crosslinkers, other UV or HEV absorbers, and diluents.

Compounds of formula I, when copolymerized with other reactivecomponents, provide polymerized products that contain chromophoricsubstituents. Such chromophoric substituents can provide the productwith desirable light absorbing properties as described above. Forinstance, ophthalmic devices, such as a contact lenses, that contain thechromophoric substituent, may block undesirable high energy light, asdescribed in detail above. Thus, the invention encompasses ophthalmicdevices that are polymerized reaction products of a reactive mixture(comprising, for instance, a hydrophilic component, and a siliconecontaining compound), wherein the polymerized reaction product contains,as covalently bound substituents, one or more chromophores of formulaIV:

wherein m and n are independently 0, 1, 2, 3, or 4; X is O, S, NR, SO,or SO₂; R at each occurrence is independently H, C₁-C₆ alkyl,cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or a link to thepolymerized reaction product; R¹ and R², when present, are independentlyat each occurrence C₁-C₆ alkyl, C₁-C₆ alkoxy, C₁-C₆ thioalkyl, C₃-C₇cycloalkyl, aryl, halo, hydroxy, amino, NR³R⁴, or benzyl, wherein R³ andR⁴ are independently H or C₁-C₆ alkyl, or two adjacent R¹ or R² groups,together with the carbon atoms to which they are attached, combine toform a cycloalkyl or aryl ring; R⁵ is a link to the polymerized reactionproduct; and EWG is an electron withdrawing group (preferably cyano).

In formula IV, X is preferably O or S. In formula IV, the link to thepolymerized reaction product preferably comprises the residue of apolymerizable group and one or more of an alkylene group, acycloalkylene group, a heterocycloalkylene group, an arylene group, aheteroarylene group, an oxaalkylene group, an alkylene-amide-alkylenegroup, or an alkylene-amine-alkylene group. Preferred polymerizablegroups include styryl, vinyl carbonate, vinyl ether, vinyl carbamate,N-vinyl lactam, N-vinylamide, (meth)acrylate, or (meth)acrylamide.

Preferred polymerized reaction products may further comprise one or morecovalently attached UV absorbing chromophores, in addition to thechromophore of formula IV. Preferred UV absorbing chromophores includethe residue of a benzophenone, a benzotriazole, a triazine, asubstituted acrylonitrile, a salicyclic acid derivative, a benzoic acidderivative, a cinnamic acid derivative, a chalcone derivative, a dypnonederivative, a crotonic acid derivative, or mixtures thereof.

Curing of Hydrogels and Manufacture of Lens

The reactive mixtures may be formed by any of the methods known in theart, such as shaking or stirring, and used to form polymeric articles ordevices by known methods. The reactive components are mixed togethereither with or without a diluent to form the reactive mixture.

For example, ophthalmic devices may be prepared by mixing reactivecomponents, and, optionally, diluent(s), with a polymerization initiatorand curing by appropriate conditions to form a product that can besubsequently formed into the appropriate shape by lathing, cutting, andthe like. Alternatively, the reactive mixture may be placed in a moldand subsequently cured into the appropriate article.

A method of making a molded ophthalmic device, such as a siliconehydrogel contact lens, may comprise: preparing a reactive monomermixture; transferring the reactive monomer mixture onto a first mold;placing a second mold on top the first mold filled with the reactivemonomer mixture; and curing the reactive monomer mixture by free radicalcopolymerization to form the silicone hydrogel in the shape of a contactlens.

The reactive mixture may be cured via any known process for molding thereactive mixture in the production of contact lenses, includingspincasting and static casting. Spincasting methods are disclosed inU.S. Pat. Nos. 3,408,429 and 3,660,545, and static casting methods aredisclosed in U.S. Pat. Nos. 4,113,224 and 4,197,266. The contact lensesof this invention may be formed by the direct molding of the siliconehydrogels, which is economical, and enables precise control over thefinal shape of the hydrated lens. For this method, the reactive mixtureis placed in a mold having the shape of the final desired siliconehydrogel and the reactive mixture is subjected to conditions whereby themonomers polymerize, thereby producing a polymer in the approximateshape of the final desired product.

After curing, the lens may be subjected to extraction to removeunreacted components and release the lens from the lens mold. Theextraction may be done using conventional extraction fluids, suchorganic solvents, such as alcohols or may be extracted using aqueoussolutions.

Aqueous solutions are solutions which comprise water. The aqueoussolutions of the present invention may comprise at least about 20 weightpercent water, or at least about 50 weight percent water, or at leastabout 70 weight percent water, or at least about 95 weight percentwater. Aqueous solutions may also include additional water solubleFormulas such as inorganic salts or release agents, wetting agents, slipagents, pharmaceutical and nutraceutical Formulas, combinations thereofand the like. Release agents are compounds or mixtures of compoundswhich, when combined with water, decrease the time required to release acontact lens from a mold, as compared to the time required to releasesuch a lens using an aqueous solution that does not comprise the releaseagent. The aqueous solutions may not require special handling, such aspurification, recycling or special disposal procedures.

Extraction may be accomplished, for example, via immersion of the lensin an aqueous solution or exposing the lens to a flow of an aqueoussolution. Extraction may also include, for example, one or more of:heating the aqueous solution; stirring the aqueous solution; increasingthe level of release aid in the aqueous solution to a level sufficientto cause release of the lens; mechanical or ultrasonic agitation of thelens; and incorporating at least one leaching or extraction aid in theaqueous solution to a level sufficient to facilitate adequate removal ofunreacted components from the lens. The foregoing may be conducted inbatch or continuous processes, with or without the addition of heat,agitation or both.

Application of physical agitation may be desired to facilitate leach andrelease. For example, the lens mold part to which a lens is adhered canbe vibrated or caused to move back and forth within an aqueous solution.Other methods may include ultrasonic waves through the aqueous solution.

The lenses may be sterilized by known means such as, but not limited to,autoclaving.

As indicated above, preferred ophthalmic devices are contact lenses,more preferably soft hydrogel contact lenses. The transmissionwavelengths and percentages described herein may be measured on variousthicknesses of lenses using, for instance, the methodologies describedin the Examples. By way of example, a preferred center thickness formeasuring transmission spectra in a soft contact lens may be from 80 to100 microns, or from 90 to 100 microns or from 90 to 95 microns.Typically, the measurement may be made at the center of the lens using,for instance, a 4 nm instrument slit width. Various concentrations ofthe one or more polymerizable high energy light absorbing compounds maybe used to achieve the transmission characteristics described above. Forinstance, the concentration may be in the range of at least 1 percent,or at least 2 percent; and up to 10 percent, or up to 5 percent, basedon the weight percentages of all components in the reactive mixture,excluding diluent. A typical concentration may be in the range of 3 to 5percent.

Silicone hydrogel ophthalmic devices (e.g., contact lenses) according tothe invention preferably exhibit the following properties. All valuesare prefaced by “about,” and the devices may have any combination of thelisted properties. The properties may be determined by methods known tothose skilled in the art, for instance as described in United Statespre-grant publication US20180037690, which is incorporated herein byreference.

Water concentration %: at least 20%, or at least 25% and up to 80% or upto 70%

Haze: 30% or less, or 10% or less

Kruss dynamic contact angle (°): 100° or less, or 50° or less

Tensile Modulus (psi): 120 or less, or 80 to 120

Oxygen permeability (Dk, barrers): at least 80, or at least 100, or atleast 150, or at least 200

Elongation to Break: at least 100

For ionic silicon hydrogels, the following properties may also bepreferred (in addition to those recited above):

Lysozyme uptake (μg/lens): at least 100, or at least 150, or at least500, or at least 700

Polyquaternium 1 (PQ1) uptake (%): 15 or less, or 10 or less, or 5 orless

Some embodiments of the invention will now be described in detail in thefollowing Examples.

EXAMPLES Test Methods

Ultraviolet-visible spectra of compounds in solution were measured on aPerkin Elmer Lambda 45 or an Agilent Cary 6000i UV/VIS scanningspectrometer. The instrument was thermally equilibrated for at leastthirty minutes prior to use. For the Perkin Elmer instrument, the scanrange was 200-800 nm; the scan speed was 960 nm per minute; the slitwidth was 4 nm; the mode was set on transmission or absorbance; andbaseline correction was selected. For the Cary instrument, the scanrange was 200-800 nm; the scan speed was 600 nm/min; the slit width was2 nm; the mode was transmission or absorbance; and baseline correctionwas selected. A baseline correction was performed before samples wereanalyzed using the autozero function.

Ultraviolet-visible spectra of contact lenses formed in part from theclaimed compositions were measured on a Perkin Elmer Lambda 45 UV/VIS oran Agilent Cary 6000i UV/VIS scanning spectrometer using packingsolution. The instrument was thermally equilibrated for at least thirtyminutes prior to use. For the Perkin Elmer instrument, the scan rangewas 200-800 nm; the scan speed was 960 nm per minute; the slit width was4 nm; the mode was set on transmission; and baseline correction wasselected. Baseline correction was performed using cuvettes containingplastic two-piece lens holders and the same solvents. These two-piececontact lens holders were designed to hold the sample in the quartzcuvette in the location through which the incident light beam traverses.The reference cuvette also contained a two-piece holder. To ensure thatthe thickness of the samples is constant, all lenses were made usingidentical molds. The center thickness of the contact lens was measuredusing an electronic thickness gauge. Reported center thickness andpercent transmission spectra are obtained by averaging three individuallens data.

It is important to ensure that the outside surfaces of the cuvette arecompletely clean and dry and that no air bubbles are present in thecuvette. Repeatability of the measurement is improved when the referencecuvette and its lens holder remain constant and when all samples use thesame sample cuvette and its lens holder, making sure that both cuvettesare properly inserted into the instrument.

The following abbreviations will be used throughout the Examples andFigures and have the following meanings:

-   BC: back or base curve plastic mold-   FC: front curve plastic mold-   DMA: N, N-dimethylacrylamide (Jarchem)-   HEMA: 2-hydroxyethyl methacrylate (Bimax)-   PVP: poly(N-vinylpyrrolidone) (ISP Ashland)-   PDMA: polydimethylacrylamide-   PVMA: polyvinylmethyacetamide-   EGDMA: ethylene glycol dimethacrylate (Esstech)-   TEGDMA: tetraethylene glycol dimethacrylate (Esstech)-   Irgacure 819: bis(2,4,6-trimethylbenzoyl)-phenylphosphineoxide (BASF    or Ciba Specialty Chemicals)-   Irgacure 1870: blend of    bis(2,6-dimethoxybenzoyl)-2,4,4-trimethyl-pentylphosphineoxide and    1-hydroxy-cyclohexyl-phenyl-ketone (BASF or Ciba Specialty    Chemicals)-   mPDMS: mono-n-butyl terminated monomethacryloxypropyl terminated    polydimethylsiloxane (M_(n)=800-1000 daltons) (Gelest)-   HO-mPDMS: mono-n-butyl terminated    mono-(2-hydroxy-3-methacryloxypropyloxy)-propyl terminated    polydimethylsiloxane (M_(n)=400-1500 daltons) (Ortec or DSM-Polymer    Technology Group)-   ac-PDMS: bis-3-acryloxy-2-hydroxypropyloxypropyl    polydimethylsiloxane (Tegomer V-Si 2250 from Evonik)-   Blue HEMA:    1-amino-4-[3-(4-(2-methacryloyloxy-ethoxy)-6-chlorotriazin-2-ylamino)-4-sulfophenylamino]anthraquinone-2-sulfonic    acid, as described in U.S. Pat. No. 5,944,853-   Da: dalton or g/mole-   kDa: kilodalton or an atomic mass unit equal to 1,000 daltons-   SiMAA: 2-propenoic acid,    2-methyl-2-hydroxy-3-[3-[1,3,3,3-tetramethyl-1-[(trimethylsilyl)oxy]disiloxanyl]propoxy]propyl    ester (Toray) or    3-(3-(1,1,1,3,5,5,5-heptamethyltrisiloxan-3-yl)propoxy)-2-hydroxypropyl    methacrylate-   RB247: 1,4-Bis[2-methacryloxyethylamino]-9,10-anthraquinone-   BHT:—butylated hydroxytoluene-   D3O: 3,7-dimethyl-3-octanol (Vigon)-   DIW: deionized water-   MeOH: methanol-   IPA: isopropyl alcohol-   HCl: hydrochloric acid-   CH₂Cl₂ or DCM: methylene chloride or dichloromethane-   SOCl₂: thionyl chloride-   mCPBA: m-chloroperbenzoic acid-   EtOAc: ethyl acetate-   NH₂CH₂CH₂OH: ethanolamine or 2-aminoethanol-   Norbloc: 2-(2′-hydroxy-5-methacrylyloxyethylphenyl)-2H-benzotriazole    (Janssen)-   PP: polypropylene which is the homopolymer of propylene-   TT: Tuftec which is a hydrogenated styrene butadiene block copolymer    (Asahi Kasei Chemicals)-   Z: Zeonor which is a polycycloolefin thermoplastic polymer (Nippon    Zeon Co Ltd)-   TL03 lights: Phillips TLK 40W/03 bulbs-   LED: light emitting diode-   ¹N NMR: proton nuclear magnetic resonance spectroscopy-   UV-VIS: ultraviolet-visible spectroscopy-   L: liter-   mL: milliliter-   Equiv. or eq.: equivalent-   kg: kilogram-   g: gram-   mol: mole-   mmol: millimole-   min: minute(s)-   nm: nanometer(s)-   TLC: thin layer chromatography-   Borate Buffered Packing Solution: 18.52 grams (300 mmol) of boric    acid, 3.7 grams (9.7 mmol) of sodium borate decahydrate, and 28    grams (197 mmol) of sodium sulfate were dissolved in enough    deionized water to fill a 2-liter volumetric flask.

Example 1 Synthesis of 2-(2-cyanoacetamido)ethyl methacrylate (A) and2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl methacrylate (B)as shown in Scheme 2

Methyl cyanoacetate (40 grams, 0.4037 mole) and 25 mL of dichloromethanewere stirred in a 3 neck, 500 mL round bottom flask under equipped witha reflux condenser under a nitrogen environment. 2-aminoethanol (23.8grams, 0.3897 mole, ˜0.97 eq.) was added to the solution via an additionfunnel, after which the temperature rose and the methylene chloridebegan to reflux. After the exotherm ceased, external heat was applied tocontinue a gentle reflux for a total of two hours, after which noethanolamine was observed by thin layer chromatography.

The reaction may also be conducted at room temperature and is completewithin a few hours.

The mixture was cooled to room temperature and all the methylenechloride was evaporated at reduced pressure. The residual oil was washedthree times with 50 mL of ethyl acetate to remove unreacted startingmaterial and non-polar impurities. The residual ethyl acetate was thenremoved under reduced pressure, and the resulting oil was used foracylation without any further purification.

The crude N-2-hydroxyethylacetamide derivative was dissolved in 150 mLof dichloromethane containing 40 grams of pyridine (˜0.5 mole) in athree-neck round bottom flask equipped with a reflux condenser, anaddition funnel, and a magnetic stirring bar. The flask was immersed inan ice bath and allowed to cool down to around 0° C. Methacryloylchloride (45.76 grams, ˜0.44 mole) was added dropwise from the additionfunnel, and the resulting reaction mixture was allowed to warm up toroom temperature while constantly stirring the system. Methanol (20 mL)was the added to the flask to quench any unreacted methacryloylchloride. The volatile components were removed by rotary evaporationunder reduced pressure, and the crude product dissolved in 800 mL ofdilute aqueous HCl. The resulting aqueous solution was extracted threetimes with 100 mL of hexanes in a separatory funnel to remove anynon-polar impurities. The organic layers were discarded. Sodium chloridewas added to the aqueous layer which was then extracted three times with300 mL of ethyl acetate. About 50 milligrams of BHT were added to thecombined organic fractions as an inhibitor, and the ethyl acetateremoved by rotary evaporation under reduced pressure. The crude productcrystalized out of solution during solvent removal. When about 100 mL ofethyl acetate was left in the flask, 250 mL of hexanes was added, andthe crude product was isolated by vacuum filtration using a frittedglass funnel. Thin layer chromatography indicated the presence of asingle compound. The filter cake was washed two times with 150 mL ofhexanes and then vacuum dried at 40° C., yielding 53 grams (about 70%yield) of 2-(2-cyanoacetamido)ethyl methacrylate (A). ¹H NMR (500 MHz,CDCl₃) δ 1.93 (3H, s, CH₃), 3.36 (2H, s, CNCH₂), 3.60 (2H, dd, CH₂NH),4.26 (2H, t, CH₂OC═O), 5.59 (1H, m, vinylic), 6.11 (1H, bs, vinylic),6.52 (1H, bs, NH).

A mixture of 9H-thioxanthene-9-one (2.12 grams, 0.01 mole) and thionylchloride (5 mL, 8.2 grams, ˜0.07 mole) was refluxed in a 50 mL roundbottom flask under a nitrogen atmosphere with constant stirring. Aftertwo hours, the red solution was evaporated to dryness ensuring that allunreacted thionyl chloride was removed from the system.2-(2-Cyanoacetamido)ethyl methacrylate (A) (2.3 grams, 0.0117 mole,˜1.17 eq.) and 15 mL of dichloromethane were added, and the resultingreaction mixture was heated to reflux under a nitrogen blanket. Thereaction was monitored by thin layer chromatography. After two hours, nochanges were observed in the chromatogram, so the reactive mixture wasallowed to cool down to room temperature.2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl methacrylate (B)was isolated as yellow crystals (3.2 grams, 82% yield) after passingthrough a short silica gel column (CH₂Cl₂, followed by 8 weight % EtOAcin CH₂Cl₂). The UV-VIS transmission spectrum of a 0.2 mM methanolsolution Compound B is shown in FIG. 1. ¹H NMR (500 MHz, CDCl₃) δ 1.84(3H, s, CH₃), 3.47 (2H, m, CH₂NH), 4.01 (2H, t, CH₂OC═O), 5.55 (1H, m,vinylic), 5.91 (1H, bs, NH), 5.98 (1H, bs, vinylic), 7.24 (1H, t, Ar—H),7.31 (1H, t, Ar—H), 7.39 (2H, m, Ar—H), 7.49 (1H, d, Ar—H), 7.55 (1H, m,Ar—H), 7.61 (1H, d, Ar—H), 8.04 (1H, m, Ar—H).

Example 2 Synthesis of2-(2-cyano-2-(9H-xanthen-9-ylidene)acetamido)ethyl methacrylate (C) asshown in Scheme 3

A mixture of 9H-xanthen-9-one (5.0 grams, 0.0255 mole) and thionylchloride (10 mL, 16.4 grams, 0.138 mole) was refluxed in a 50 mL roundbottom flask under a nitrogen atmosphere with constant stirring. Afterthree hours, the red solution was evaporated to dryness ensuring thatall unreacted thionyl chloride was removed from the system.2-(2-cyanoacetamido)ethyl methacrylate (A) (6.0 grams, 0.0306 mole, ˜1.2eq.) and 20 mL of dichloromethane were added and the resulting reactionmixture was heated to reflux under a nitrogen blanket. The reaction wasmonitored by thin layer chromatography. The mixture was cooled to roomtemperature after 2.5 hours and2-(2-cyano-2-(9H-xanthen-9-ylidene)acetamido)ethyl methacrylate (C)purified after passing through a short silica gel column (CH₂Cl₂, andethyl acetate in CH₂Cl₂). The off-white precipitate formed during rotaryevaporation is washed with hexane and dried in a vacuum oven at 40° C.overnight. The UV-VIS transmission spectrum of Compound (C) is shown inFIG. 1 in a 0.2 mM methanol solution. ¹H NMR (500 MHz, CDCl₃) δ 1.85(3H, s, CH₃), 3.60 (2H, dd, CH₂NH), 4.2 (2H, t, CH2OC═O), 5.53 (1H, t,vinylic), 5.99 (1H, bs, vinylic), 6.17 (1H, t, NH), 7.12 (1H, t, Ar—H),7.29-7.34 (3H, m, Ar—H), 7.45 (1H, ddd, Ar—H), 7.52 (1H, ddd, Ar—H),7.67 (1H, dd, Ar—H), 8.41 (1H, dd, Ar—H).

Example 3 Synthesis of2-(2-cyano-2-(10-methylacridin-9(10H)-ylidene)acetamido)ethylmethacrylate (D) as shown in Scheme 4 (Prophetic)

A mixture of 10-methylacridin-9(10H)-one (2.09 grams, 0.01 mole) andthionyl chloride (5 mL, 8.2 grams, ˜0.07 mole) is refluxed in a 50 mLround bottom flask under a nitrogen atmosphere with constant stirring.After two hours, the solution is evaporated to dryness ensuring that allunreacted thionyl chloride is removed from the system.2-(2-cyanoacetamido)ethyl methacrylate (A) (2.3 grams, 0.0117 mole,˜1.17 eq.) and 15 mL of dichloromethane are added and the resultingreaction mixture is heated to reflux under a nitrogen blanket. Thereaction is monitored by thin layer chromatography. When no changes areobserved in the chromatogram, the reactive mixture is allowed to cooldown to room temperature.2-(2-cyano-2-(10-methylacridin-9(10H)-ylidene)acetamido)ethylmethacrylate (D) may be isolated by known methods, for instance afterpassing through a short silica gel column.

Example 4 Synthesis of2-(2-cyano-2-(10,10-dioxido-9H-thioxanthen-9-ylidene)acetamido)ethylmethacrylate (E) as shown in Scheme 5

To a chilled solution of2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl methacrylate (B)(2.0 grams, 5.2 mmol) in dichloromethane, 2.32 grams ofm-chloroperbenzoic acid (75% purity, ˜2 eq., mCPBA) were added. Themixture was stirred cold for one hour and then allowed to warm up toroom temperature. The solution lost its yellow color as the reactionproceeded, and a white solid crystallized or precipitated out ofsolution. The volatiles were evaporated under reduced pressure. Theresidue was re-dissolved in ethyl acetate and extracted with diluteaqueous base, followed by dilute aqueous saline solutions. The organiclayer was separated, and the solvent removed by rotary evaporation underreduced pressure. The residue was washed with hexanes over a frittedglass funnel and vacuum dried. The UV-VIS transmission spectrum of a 0.2mM methanolic solution of Compound E is shown in FIG. 1. ¹H NMR (500MHz, CDCl₃) δ 1.85 (3H, s, CH₃), 3.35 (1H, m, CH₂NH), 3.61 (1H, m,CH₂NH), 3.81 (1H, m, CH₂OC═O), 4.05 (1H, m, CH₂OC═O), 5.55 (1H, m,vinylic), 5.95 (1H, m, vinylic), 6.35 (1H, bs, NH), 7.5-7.75 (5H, m,Ar—H), 8.03 (2H, t, Ar—H), 8.12 (1H, d, Ar—H).

Example 5 Synthesis of 2-(2-cyanoacetamido)ethyl methacrylate (F) andN-(2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl) methacrylate(G) as shown in Scheme 6

Methyl cyanoacetate (22 grams, 0.22 mole) and 250 mL of dichloromethanewere stirred in a 3 neck, 500 mL round bottom flask under equipped witha reflux condenser under a nitrogen environment. The solution is cooledin a water bath and 1,2-diaminoethane (12 grams, 0.2 mole, ˜0.9 eq.)added to the mixture. As the reaction progresses, the mixture appearsmore and more heterogenous, with the product crashing out of solution.After four hours of stirring at room temperature, the volatiles areevaporated under reduced pressure and the residue is washed with ethylacetate over a fritted glass funnel and dried at 50° C. prior to furtheruse. ¹H NMR (500 MHz, D₂O) δ 2.74 (2H, t, CH₂NH₂), 3.29 (2H, t, CH₂NH),3.38 (2H, s, CH₂CN).

2-aminoethyl cyanoacetamide (12.7 g, 0.1 mole) and 12.0 grams of sodiumcarbonate are stirred in 150 mL of methanol while being chilled in anice bath. Methacryloyl chloride (11.5 g, 1.1 eq.) is added to thesuspension in a dropwise manner, while maintaining the reactiontemperature below 30° C. at all times. Once the reaction is complete,evaporate all volatiles under reduced pressure, redissolve the productin acetonitrile and filter the solution to remove all the salts present.Evaporate the acetonitrile under reduced pressure and wash the resultingsolids with ethyl acetate over a fritted glass funnel to obtain thedesired 2-(2-cyanoacetamido)ethyl methacrylamide (F). ¹H NMR (500 MHz,CD₃OD) δ 1.86 (3H, s, CH₃), 3.22-3.26 (4H, m, NH, CH₂CN), 3.29 (4H, m,CH₂NH), 5.31 (1H, m, vinylic), 5.63 (1H, m, vinylic).

A mixture of thioxanthone (4.24 grams, 0.02 mole) and 8 mL of thionylchloride (13.12 grams, ˜0.11 mole) was gently refluxed under a nitrogenatmosphere with constant stirring. After two hours of heating, thesolution was evaporated to dryness under reduced pressure, ensuring thatall unreacted thionyl chloride was removed. 2-(2-cyanoacetamido)ethylmethacrylamide (F) (4.2 grams, ˜1.1 eq.) and 20 mL of degassed methylenechloride were added to the flask, and the mixture was gently refluxedfor 3 hours under a nitrogen environment, while monitoring the progressby TLC. The volatiles were evaporated under reduced pressure, and theorganics are washed with ethyl acetate. Large quantities of aprecipitate enriched with the major product were observed. Thesuspension was filtered, and the residual solids washed with ethylacetate prior to drying in a vacuum oven. The UV-VIS transmissionspectrum of a 0.2 mM methanolic solution of Compound G is shown in FIG.2. ¹H NMR (500 MHz, CDCl₃) δ 1.89 (3H, s, CH₃), 3.26 (2H, m, CH₂NH),3.32 (2H, m, CH₂NH), 5.33 (1H, m, vinylic), 5.68 (1H, m, vinylic), 6.63(1H, m, NH), 6.49 (1H, m, NH), 7.25 (1H, m, Ar—H), 7.33 (1H, dt, Ar—H),7.39 (2H, m, Ar—H), 7.51-7.59 (3H, m, Ar—H), 8.05 (1H, m, Ar—H).

Example 6N-(2-(2-cyano-2-(10-methylacridin-9(10H)ylidene)acetamido)ethyl)-methacrylamide(H) as shown in Scheme 7

N-(2-Aminoethyl)-2-cyanoacetamide (2): Compound 1 (30 g, 303 mmol, 1.0equiv) was added to a solution of ethylene diamine (54.5 g, 909 mol, 3equiv) in dichloromethane (600 mL) at −20° C. over 30 minutes. Thereaction was warmed to room temperature over 2 hours and stirred for 3hours, at which point LC-MS indicated the reaction was complete. Theresulting precipitate was filtered and washed with dichloromethane(2×100 mL) to give compound 2 (25 g, 66% yield, >95% purity) as a whitesolid.

N-(2-(2-Cyanoacetamido)ethyl)methacrylamide (3): A solution ofmethylacrylic anhydride (41 g, 264 mmol, 1.3 equiv) and triethylamine(40 mL, 287 mmol, 1.3 equiv) in dichloromethane (300 mL) was stirred atroom temperature for 1 hour. The reaction was cooled to 0° C. andcompound 2 (28 g, 220 mmol, 1.0 equiv) was added portionwise to thereaction mixture at 0° C. The reaction was warmed to room temperatureand stirred for 5 hours, at which point LC-MS indicated the reaction wascomplete. The resulting precipitate was filtered and washed withdichloromethane (2×100 mL) to give compound 3 (25.1 g, 60% yield, >95%purity) as a white solid.

9,9-Dichloro-10-methyl-9,10-dihydroacridine (5): Compound 4 (10 g, 4.85mmol, 1.0 equiv) in thionyl chloride (200 mL, 2.75 mol, 55 equiv) wasstirred at 60° C. for 2 hours, at which point ¹H-NMR indicated thereaction was complete. The thionyl chloride was removed under reducedpressure. The residue was azeotroped with toluene (2×20 mL) to givecrude compound 5 as a yellow solid (12.5 g), which was usedsubsequently.

N-(2-(2-Cyano-2-(10-methylacridin-9(10H)-ylidene)acetamido)ethyl)methacryl amide (H): Triethylamine (20 mL, 143 mmol, 3.0 equiv) wasadded dropwise to a solution of the crude compound 5 (12.5 g, 48.5 mmol,1.0 equiv) and compound 3 (9.33 g, 48.5 mmol. 1.0 equiv) in 1 to 1mixture of dichloromethane and acetonitrile (200 mL) at 0° C. over 30minute. The reaction was warmed to room temperature and stirred for 2hours, at which point LC-MS indicated the reaction was complete. Themixture was passed through a plug of silica gel (150 g), eluting withdichloromethane (500 mL). The organics were concentrated under reducedpressure. The residue was purified over silica gel (800 g), eluting withethyl acetate, to give compound (H) as a yellow solid. The solid wastriturated with methyl tert-butyl ether (2×200 mL) for 2 hours. Thesolid was collected by filtration and triturated with chloroform (50 mL)for 30 minutes to give the pure compound (H) (11.9 g, 60% yield from twosteps, 97.5% purity) as a yellow solid.

The UV-VIS transmission spectrum of a 0.2 mM methanolic solution ofCompound H is shown in FIG. 2. ¹H NMR (500 MHz, DMSO-d₆) δ 1.87 (3H, m,CH₃), 3.15-3.20 (4H, m, CH₂NH), 3.72 (3H, s, CH₃N), 5.36 (1H, s,vinylic), 5.68 (1H, m, vinylic), 7.14 (1H, bt, NH), 7.29 (1H, bt, NH,7.49-7.65 (4H, m, Ar—H), 8.02-8.81 (4H, Ar—H).

Example 7 Synthesis of 2-(2-cyanoacetamido)ethyl acrylamide (I) andN-(2-(2-cyano-2-(9H-xanthen-9-ylidene)acetamido)ethyl)acrylamide (J) asshown in Scheme 8

2-(2-Cyanoacetamido)ethyl acrylamide (I) was prepared by the samemethodology as used for 2-(2-cyanoacetamido)ethyl methacrylate (F).2-aminoethyl cyanoacetamide (12.7 g, 0.1 mole) and 12.0 grams of sodiumcarbonate are stirred in 150 mL of methanol while being chilled in anice bath. Acryloyl chloride (9.9 g, 1.1 eq.) is added to the suspensionin a dropwise manner, while maintaining the reaction temperature below30° C. at all times. Once the reaction is complete, evaporate allvolatiles under reduced pressure, redissolve the product in acetonitrileand filter the solution to remove all the salts present. Evaporate theacetonitrile under reduced pressure and wash the resulting solids withethyl acetate over a fritted glass funnel to obtain the desired2-(2-cyanoacetamido)ethyl acrylamide(I). ¹H NMR (500 MHz, CD₃OD) δ3.22-3.31 (8H, m, NH, CH₂), 5.59 (1H, dd, vinylic), 6.14 (2H, dd,vinylic).

A mixture of xanthone (3.92 grams, 0.02 mole) and 5 mL of thionylchloride (8.2 grams, ˜0.07 mole) in 10 mL of toluene was gently refluxedunder a nitrogen atmosphere with constant stirring. After six hours ofheating, the solution cooled and volatiles were evaporated under reducedpressure, ensuring that all unreacted thionyl chloride was removed fromthe system. 2-(2-cyanoacetamido)ethyl acrylamide (I) (3.8 grams, ˜1.05eq.) and 20 mL of methylene chloride were added to the flask, and themixture was gently refluxed for 3 hours under a nitrogen environment,while monitoring the progress by TLC. Volatile components wereevaporated under reduced pressure. The residue was washed with warmethyl acetate and filtered over a fritted glass funnel. The filter cakewas washed with additional ethyl acetate, followed by water. Thelight-yellow solid was dried in a vacuum oven. The UV-VIS transmissionspectrum of a 0.2 mM methanolic solution of Compound J is shown in FIG.2. ¹H NMR (500 MHz, DMSO-d₆) δ 3.15-3.25 (4H, m, CH₂), 5.62 (1H, dd,vinylic), 6.08-6.23 (2H, m, vinylic), 7.32-7.75 (1H, dt, Ar—H),7.46-7.72 (6H, Ar—H), 8.17 (1H, bt, NH), 8.34 (1H, dd, Ar—H), 8.88 (1H,bt, NH).

Example 8 Synthesis of 2-(2-cyanoacetoxy)ethyl methacrylate (K) and2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetoxy)ethyl methacrylate (L) asshown in Scheme 9

2-(2-Cyanoacetoxy)ethyl methacrylate (K) was prepared by couplingcyanoacetic acid with 2-hydroxyethyl methacrylate as follows.Cyanoacetic acid (9 g, 0.106 mole) and 13 g of 2-hydroxyethylmethacrylate (HEMA, are stirred in 250 mL of dichloromethane, and ethyldimethylaminopropyl carbodiimide hydrochloride (EDC) is added to thesuspension in 4 batches of 5 grams each (20 g, 0.104 mole). The mixturegradually becomes more homogenous as the less polar derivative is formedand volatiles are evaporated under reduced pressure after completion ofthe reaction. The product is redissolved in a 25:75 mixture of ethylacetate and hexanes by weight and extracted several times with deionizedwater to remove any residual salts and unreacted HEMA. A small amount of4-methoxyhydroquinone (<20 mg) is added to the organic layer and theproduct is obtained pure after evaporation of the solvents under reducedpressure. ¹H NMR (500 MHz, CDCl₃) δ 1.92 (3H, m, CH₃), 3.47 (2H, S,NCCH₂), 4.36 (2H, m, OCH₂), 4.44 (2H, m, OCH₂), 4.59 (1H, m, vinylic),6.10 (1H, m, vinylic).

A mixture of thioxanthone (4.24 grams, 0.02 mole) and 8 mL of thionylchloride (13.12 grams, ˜0.11 mole) was gently refluxed under a nitrogenatmosphere with constant stirring. After two hours of heating, thesolution was evaporated to dryness under reduced pressure, ensuring thatall unreacted thionyl chloride was removed. A solution of2-(2-cyanoacetoxy)ethyl methacrylate (K) (4.33 grams, ˜1.1 eq.) in 20 mLof degassed methylene chloride was added to the flask, and the mixturewas gently refluxed for 3 hours under a nitrogen environment, whilemonitoring the progress by TLC. The residue was washed with methanol toremove most of the unreacted starting thioxanthone, re-concentrated, andthe crude product was purified by chromatography over a silica gel plugand vacuum dried overnight. The UV-VIS transmission spectrum of a 0.2 mMsolution of Compound L in dichloromethane is shown in FIG. 2. ¹H NMR(500 MHz, CDCl₃) δ 1.92 (3H, s, CH₃), 4.36 (2H, m, CH₂), 4.44 (2H, m,CH₂), 5.59 (1H, m, vinylic), 6.10 (1H, m, vinylic), 7.24-7.62 (7H, m,Ar—H), 8.1 (1H, m, Ar—H).

Example 9 Silicone Hydrogel Formulations Comprising Compound (B)

Reactive monomer mixtures were prepared composed of 77 weight percent ofthe formulations listed in Table 4 and 23 weight percent of the diluentD3O. The reactive monomer mixtures were individually filtered through a3 μm filter using a stainless-steel syringe under pressure.

TABLE 4 Ex 9A Ex 9B Ex 9C Ex 9D Component (weight %) (weight %) (weight%) (weight %) mPDMS 1000 30.85 30.7 30.55 30.39 SiMAA 27.61 27.48 27.3527.2 DMA 23.76 23.6 23.53 23.4 HEMA 5.94 5.91 5.88 5.85 TEGDMA 1.52 1.521.51 1.5 PVP K90 6.9 6.9 6.8 6.8 Irgacure 1870 0.35 0.34 0.34 0.34 RB2470.02 0.02 0.02 0.02 Compound (B) 3.05 3.03 3.02 3 Norbloc ® 0 0.5 1 1.5Σ Components 100 100 100 100

Formulations 9A-9D were degassed at ambient temperature by applyingvacuum (40 torr) for 45 minutes. Then, in a glove box with a nitrogengas atmosphere and less than about 0.1-0.2 percent oxygen gas, about 75μL of the reactive mixture were dosed using an Eppendorf pipet at roomtemperature into the FC made of 90:10 (w/w) Zeonor/TT blend. The BC madeof 90:10 (w/w) Z:TT blend was then placed onto the FC. The molds wereequilibrated for a minimum of twelve hours in the glove box prior todosing. Pallets containing eight mold assemblies each were transferredinto an adjacent glove box maintained at 65° C., and the lenses werecured from the top and the bottom for 15 minutes using 435 nm LED lightshaving an intensity of about 2 mW/cm² at the tray's location.

The lenses were manually de-molded with most lenses adhering to the FCand released by suspending the lenses in about one liter of 70 percentIPA for about one hour, followed by soaking two more times with fresh 70percent IPA for 30 minutes; then two times with fresh DIW for 15minutes; then two time with packing solution for 30 minutes. The lenseswere equilibrated and stored in borate buffered packaging solution. Aperson of ordinary skill recognizes that the exact lens release processcan be varied depending on the lens formulation and mold materials,regarding the concentrations of the aqueous isopropanol solutions, thenumber of washings with each solvent, and the duration of each step. Thepurpose of the lens release process is to release all of the lenseswithout defects and transition from diluent swollen networks to thepackaging solution swollen hydrogels. The average center thickness ofeach lens set was measured; 9A=87.7 microns, 9B=85.3 microns, 9C=87.3microns, and 9D=85.7 microns.

FIGS. 3-5 show the UV-VIS spectra of the lenses made from Formulations9A-9D demonstrating that compound (B) or combinations of compound (B)and Norbloc® may provide complete or nearly complete absorption between300 nm and 400 nm with some absorption in the high energy visible regionbetween 400 nm and 450 nm.

Example 10 Silicone Hydrogel Formulations Comprising Compounds (B) and(C)

Reactive monomer mixtures were prepared composed of 77 weight percent ofthe formulations listed in Table 5 and 23 weight percent of the diluentD3O. The reactive monomer mixtures were individually filtered through a3 μm filter using a stainless-steel syringe under pressure.

TABLE 5 Ex 10A Ex 10B Ex 10C Ex 10D Component (weight %) (weight %)(weight %) (weight %) mPDMS 1000 30.87 30.69 30.51 30.33 SiMAA 27.6627.5 27.34 27.18 DMA 23.83 23.7 23.57 23.44 HEMA 5.98 5.95 5.92 5.89TEGDMA 1.5 1.5 1.5 1.5 PVP K90 6.8 6.8 6.8 6.8 Irgacure 1870 0.34 0.340.34 0.34 RB247 0.02 0.02 0.02 0.02 Compound (B) 0 3 3 3 Compound (C) 30.5 1 1.5 Σ Components 100 100 100 100

Formulations 10A-10D were degassed at ambient temperature by applyingvacuum (40 torr) for 45 minutes. Then, in a glove box with a nitrogengas atmosphere and less than about 0.1-0.2 percent oxygen gas, about 75μL of the reactive mixture were dosed using an Eppendorf pipet at roomtemperature into the FC made of 90:10 (w/w) Zeonor/TT blend. The BC madeof 90:10 (w/w) Z:TT blend was then placed onto the FC. The molds wereequilibrated for a minimum of twelve hours in the glove box prior todosing. Pallets containing eight mold assemblies each were transferredinto an adjacent glove box maintained at 65° C., and the lenses werecured from the top and the bottom for 15 minutes using 435 nm LED lightshaving an intensity of about 2 mW/cm² at the tray's location.

The lenses were manually de-molded with most lenses adhering to the FCand released by suspending the lenses in about one liter of 70 percentIPA for about one hour, followed by soaking two more times with fresh 70percent IPA for 30 minutes; then two times with fresh DIW for 15minutes; then two time with packing solution for 30 minutes. The lenseswere equilibrated and stored in borate buffered packaging solution. Aperson of ordinary skill recognizes that the exact lens release processcan be varied depending on the lens formulation and mold materials,regarding the concentrations of the aqueous isopropanol solutions, thenumber of washings with each solvent, and the duration of each step. Thepurpose of the lens release process is to release all of the lenseswithout defects and transition from diluent swollen networks to thepackaging solution swollen hydrogels. The average center thickness ofeach lens set was measured; 10A=93.7 microns, 10B=93.7 microns, 10C=95.3microns, and 10D=92.3 microns.

FIGS. 6-8 show the UV-VIS spectra of the lenses made from Formulations10A-10D demonstrating that combinations of compounds (B) and (C) mayprovide complete or nearly complete absorption between 300 nm and 400 nmwith some absorption in the high energy visible region between 400 nmand 450 nm. The figures also demonstrate that compound (C) aloneprovides absorption at various wavelength ranges.

Example 11

Lenses were made using the reactive monomer mixture comprising thecomponents listed as 9D in Table 4 and same curing and hydration stepsexcept that the oxygen gas concentration in the glove box was less than0.5%. Lenses were packaged in glass vials containing PS and then placedeither on a window sill with direct sunlight (11A) or on top of acabinet without exposure to direct sunlight, only indoor lighting (11B).Controls were stored in the dark. After 3, 5, 9, 15, and 21 weeks ofexposure, UV-Visible transmission spectra of the lenses were measured asshown in FIG. 9 and FIG. 10.

For lenses exposed to direct sunlight, the absorption of high energyvisible light between 400 nm and 450 nm did not change over time. Therewere minor (about 1%) changes in the UV-VIS transmission spectra between450 nm and 700 nm over the duration of the study.

For lenses exposed to indoor lighting, the absorption of high energyvisible light between 400 nm and 450 nm did not change over time. TheUV-VIS transmission spectra did not change more than about 2% or 3%between 450 nm and 700 nm over the duration of the study.

Examples 12-25 are Prophetic Example 12(Z)-2-(2-cyano-2-(3-hydroxyacridin-9(10H)-ylidene)acetamido)ethylmethacrylate

The title compound can be synthesized by analogous procedures to thosedescribed above, starting from 3-hydroxyacridone (CAS reg. no.20168-55-2).

Example 13 2-(2-cyano-2-(10-methylacridin-9(10H)-ylidene)acetamido)ethylmethacrylate

The title compound can be synthesized by analogous procedures to thosedescribed above, starting from N-methylacridone (719-54-0).

Example 142-(2-cyano-2-(3,6-dihydroxyacridin-9(10H)-ylidene)acetamido)ethylmethacrylate

The title compound can be synthesized by analogous procedures to thosedescribed above, starting from 3,6-dihydroxyacridone (122105-95-7).

Example 15(E)-2-(2-(7H-benzo[c]xanthen-7-ylidene)-2-cyanoacetamido)ethylmethacrylate

The title compound can be synthesized by analogous procedures to thosedescribed above, starting from benzo[C]xanthone (63154-69-8).

Example 16(Z)-2-(2-cyano-2-(3-methoxy-9H-xanthen-9-ylidene)acetamido)ethylmethacrylate

The title compound can be synthesized by analogous procedures to thosedescribed above, starting from 3-methoxyxanthone (3722-52-9).

Example 172-(2-cyano-2-(3,6-dihydroxy-9H-xanthen-9-ylidene)acetamido)ethylmethacrylate

The title compound can be synthesized by analogous procedures to thosedescribed above, starting from 3,6-dihydroxyxanthone (1214-24-0).

Example 18:(E)-2-(2-cyano-2-(2-methyl-9H-xanthen-9-ylidene)acetamido)ethylmethacrylate

The title compound can be synthesized by analogous procedures to thosedescribed above, starting from 2-methylxanthone (2680-45-1).

Example 19(E)-2-(2-cyano-2-(1-hydroxy-9H-xanthen-9-ylidene)acetamido)ethylmethacrylate

The title compound can be synthesized by analogous procedures to thosedescribed above, starting from 1-hydroxyxanthone (19-41-5).

Example 20(E)-2-(2-cyano-2-(2,4-dichloro-9H-thioxanthen-9-ylidene)acetamido)ethylmethacrylate

The title compound can be synthesized by analogous procedures to thosedescribed above, starting from 2,4-dichlorothioxanthone.

Example 21(E)-2-(2-(2-chloro-9H-thioxanthen-9-ylidene)-2-cyanoacetamido)ethylmethacrylate

The title compound can be synthesized by analogous procedures to thosedescribed above, starting from 2-chlorothioxanthone.

Example 22(E)-2-(2-cyano-2-(2-isopropyl-9H-thioxanthen-9-ylidene)acetamido)ethylmethacrylate and(E)-2-(2-cyano-2-(4-isopropyl-9H-thioxanthen-9-ylidene)acetamido)ethylmethacrylate

The title compounds can be synthesized as a mixture by analogousprocedures to those described above, starting from a mixture of 2 and4-isopropyl thioxanthone.

Examples 23-25

Contact lenses from the silicone hydrogel formulations shown in Table 6can be prepared using analogous procedures to those described in Example6. In these examples, 77 weight percent of the formulations listed inTable 6 are diluted with 23 weight percent of diluent (e.g., D3O).

TABLE 6 Ex 23 Ex. 24 Ex. 25 Component (weight %) (weight %) (weight %)OH-mPDMS (n = 15) 28.00 28.50 28.00 OH-mPDMS (n = 4) 25.00 25.50 25.00ac-PDMS 5.00 4.00 5.00 DMA 24.00 20.00 20.00 HEMA 7.98 7.98 7.98 BlueHEMA 0.02 0.02 0.02 PDMA (M_(w) = 740 kDa) 5.00 0 0 PVP K90 0 7.00 9.00PVMA (M_(w) = 570 kDa) 0 2.00 0 EGDMA 0.25 0.25 0.25 Compound (B) 3.003.00 3.00 Norbloc ® or compound (C) 1.50 1.50 1.50 Irgacure 1870 0.250.25 0.25 Σ Components 100 100 100

1. A compound of formula I:

wherein: m and n are independently 0, 1, 2, 3, or 4; T is a bond, O, orNR; X is O, S, NR, SO, or SO₂; Y is a linking group; P_(g) is apolymerizable group; R at each occurrence is independently H, C₁-C₆alkyl, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or Y—P_(g); R¹and R², when present, are independently at each occurrence C₁-C₆ alkyl,C₁-C₆ alkoxy, C₁-C₆ thioalkyl, C₃-C₇ cycloalkyl, aryl, halo, hydroxy,amino, NR³R⁴, or benzyl, wherein R³ and R⁴ are independently H or C₁-C₆alkyl, or two adjacent R¹ or R² groups, together with the carbon atomsto which they are attached, combine to form a cycloalkyl or aryl ring;and EWG is an electron withdrawing group.
 2. The compound of claim 1wherein m and n are each independently 0 or
 1. 3. The compound of claim1 wherein Y at each occurrence is independently alkylene, cycloalkylene,heterocycloalkylene, arylene, heteroarylene, oxaalkylene,alkylene-amide-alkylene, alkylene-amine-alkylene, or combinationsthereof.
 4. The compound of claim 1 wherein P_(g) comprises styryl,vinyl carbonate, vinyl ether, vinyl carbamate, N-vinyl lactam,N-vinylamide, (meth)acrylate, or (meth)acrylamide.
 5. The compound ofclaim 1 wherein X is O.
 6. The compound of claim 1 wherein X is S. 7.The compound of claim 1 wherein EWG is cyano, amide, ester, keto, oraldehyde.
 8. The compound of claim 1 wherein EWG is cyano.
 9. Thecompound of claim 1 that is:2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl methacrylate;2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl acrylate;N-(2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl)methacrylamide;N-(2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)ethyl)acrylamide;2-(2-cyano-N-methyl-2-(9H-thioxanthen-9-ylidene)acetamido)ethylmethacrylate;2-cyano-2-(9H-thioxanthen-9-ylidene)-N-(2-(N-vinylacetamido)ethyl)acetamide;2-(2-cyano-2-(9H-xanthen-9-ylidene)acetamido)ethyl methacrylate;2-(2-cyano-2-(9H-xanthen-9-ylidene)acetamido)ethyl acrylate;N-(2-(2-cyano-2-(9H-xanthen-9-ylidene)acetamido)ethyl)methacrylamide;N-(2-(2-cyano-2-(9H-xanthen-9-ylidene)acetamido)ethyl)acrylamide;2-(2-cyano-N-methyl-2-(9H-xanthen-9-ylidene)acetamido)ethylmethacrylate;2-cyano-N-(2-(N-vinylacetamido)ethyl)-2-(9H-xanthen-9-ylidene)acetamide;2-(2-(acridin-9(10H)-ylidene)-2-cyanoacetamido)ethyl acrylate;N-(2-(2-(acridin-9(10H)-ylidene)-2-cyanoacetamido)ethyl)methacrylamide;N-(2-(2-(acridin-9(10H)-ylidene)-2-cyanoacetamido)ethyl)acrylamide;2-(2-(acridin-9(10H)-ylidene)-2-cyano-N-methylacetamido)ethylmethacrylate;2-(acridin-9(10H)-ylidene)-2-cyano-N-(2-(N-vinylacetamido)ethyl)acetamide;2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetamido)-2-methylpropylmethacrylate; 2-(2-cyano-2-(9H-xanthen-9-ylidene)acetoxy)-2-methylpropylacrylate;(Z)-2-(2-cyano-2-(3-hydroxyacridin-9(10H)-ylidene)acetamido)ethylmethacrylate;2-(2-cyano-2-(10-methylacridin-9(10H)-ylidene)acetamido)ethylmethacrylate;2-(2-cyano-2-(3,6-dihydroxyacridin-9(10H)-ylidene)acetamido)ethylmethacrylate;(E)-2-(2-(7H-benzo[c]xanthen-7-ylidene)-2-cyanoacetamido)ethylmethacrylate;(Z)-2-(2-cyano-2-(3-methoxy-9H-xanthen-9-ylidene)acetamido)ethylmethacrylate;2-(2-cyano-2-(3,6-dihydroxy-9H-xanthen-9-ylidene)acetamido)ethylmethacrylate;(E)-2-(2-cyano-2-(2-methyl-9H-xanthen-9-ylidene)acetamido)ethylmethacrylate;(E)-2-(2-cyano-2-(1-hydroxy-9H-xanthen-9-ylidene)acetamido)ethylmethacrylate;(E)-2-(2-cyano-2-(2,4-dichloro-9H-thioxanthen-9-ylidene)acetamido)ethylmethacrylate;(E)-2-(2-(2-chloro-9H-thioxanthen-9-ylidene)-2-cyanoacetamido)ethylmethacrylate;(E)-2-(2-cyano-2-(2-isopropyl-9H-thioxanthen-9-ylidene)acetamido)ethylmethacrylate;(E)-2-(2-cyano-2-(4-isopropyl-9H-thioxanthen-9-ylidene)acetamido)ethylmethacrylate; 2-(3-oxo-2-(9H-thioxanthen-9-ylidene)propanamido)ethylmethacrylate; 2-(3-oxo-2-(9H-thioxanthen-9-ylidene)butanamido)ethylmethacrylate;2-(3-methoxy-3-oxo-2-(9H-thioxanthen-9-ylidene)propanamido)ethylmethacrylate;2-(3-amino-3-oxo-2-(9H-thioxanthen-9-ylidene)propanamido)ethylmethacrylate2-(2-cyano-2-(10,10-dioxido-9H-thioxanthen-9-ylidene)acetamido)ethylmethacrylate;N-(2-(2-cyano-2-(10-methylacridin-9(10H)ylidene)acetamido)ethyl)methacrylamide; or 2-(2-cyano-2-(9H-thioxanthen-9-ylidene)acetoxy)ethylmethacrylate.
 10. An ophthalmic device that is a free radical reactionproduct of a reactive mixture comprising: one or more monomers suitablefor making the ophthalmic device; and a polymerizable high energy lightabsorbing compound comprising a compound of claim
 1. 11. The ophthalmicdevice of claim 10 further comprising a second polymerizable high energylight absorbing compound.
 12. The ophthalmic device of claim 11 whereinthe second polymerizable high energy light absorbing compound is a UVabsorbing compound.
 13. The ophthalmic device of claim 12 wherein the UVabsorbing compound comprises a compound of formula I, a benzophenone, abenzotriazole, a triazine, a substituted acrylonitrile, a salicyclicacid derivative, a benzoic acid derivative, a cinnamic acid derivative,a chalcone derivative, a dypnone derivative, a crotonic acid derivative,or mixtures thereof.
 14. The ophthalmic device of claim 10 wherein thepolymerizable high energy light absorbing compound comprises a mixtureof a compound of formula I wherein X is S and a compound of formula Iwherein X is O.
 15. The ophthalmic device of claim 10 wherein thepolymerizable high energy light absorbing compound comprises a mixtureof a compound of formula I wherein X is S and a benzotriazole UVabsorbing compound.
 16. The ophthalmic device of claim 10 wherein themonomer suitable for making the ophthalmic device comprises ahydrophilic component, a silicone-containing component, or mixturesthereof.
 17. The ophthalmic device of claim 10 that is a contact lens, acorneal onlay, a corneal inlay, an intraocular lens, or an overlay lens.18. The ophthalmic device of claim 10 that is a hydrogel contact lens.19. A method for making an ophthalmic device, the method comprising: (a)providing a reactive mixture containing a compound according to claim 1,one or more device forming monomers, and a radical initiator; and (b)polymerizing the reactive mixture to form the ophthalmic device.
 20. Anophthalmic device that is a reaction product of a reactive mixturecomprising: a polymerizable high energy light absorbing compound; andone or more monomers suitable for making an ophthalmic device, whereinthe ophthalmic device transmits: 45 percent or less of light having awavelength of 280 to 399 nm; from 1 percent to 70 percent of lighthaving a wavelength of 400 to 409 nm; and at least 80 percent of lighthaving a wavelength of 450 to 800 nm.
 21. The ophthalmic device of claim20 that further transmits: from 10 percent to 95 percent of light havinga wavelength of 410 to 424 nm; and at least 50 percent of light having awavelength of 425 to 449 nm.
 22. The ophthalmic device of claim 20 thattransmits: 20 percent or less of light having a wavelength of 280 to 399nm; from 3 percent to 70 percent of light having a wavelength of 400 to409 nm; and at least 85 percent of light having a wavelength of 450 to800 nm.
 23. The ophthalmic device of claim 20 wherein the polymerizablehigh energy light absorbing compound comprises a compound of formula I:

wherein: m and n are independently 0, 1, 2, 3, or 4; T is a bond, O, orNR; X is O, S, NR, SO, or SO₂; Y is a linking group; P_(g) is apolymerizable group; R at each occurrence is independently H, C₁-C₆alkyl, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or Y—P_(g); R¹and R², when present, are independently at each occurrence C₁-C₆ alkyl,C₁-C₆ alkoxy, C₁-C₆ thioalkyl, C₃-C₇ cycloalkyl, aryl, halo, hydroxy,amino, NR³R⁴, or benzyl, wherein R³ and R⁴ are independently H or C₁-C₆alkyl, or two adjacent R¹ or R² groups, together with the carbon atomsto which they are attached, combine to form a cycloalkyl or aryl ring;and EWG is an electron withdrawing group.
 24. The ophthalmic device ofclaim 23 further comprising a second polymerizable high energy lightabsorbing compound.
 25. The ophthalmic device of claim 24 wherein thesecond polymerizable high energy light absorbing compound is a UVabsorbing compound.
 26. The ophthalmic device of claim 25 wherein the UVabsorbing compound comprises a compound of formula I, a benzophenone, abenzotriazole, a triazine, a substituted acrylonitrile, a salicyclicacid derivative, a benzoic acid derivative, a cinnamic acid derivative,a chalcone derivative, a dypnone derivative, a crotonic acid derivative,or mixtures thereof.
 27. The ophthalmic device of claim 23 wherein thepolymerizable high energy light absorbing compound comprises a mixtureof a compound of formula I wherein X is S and a compound of formula Iwherein X is O.
 28. The ophthalmic device of claim 23 wherein thepolymerizable high energy light absorbing compound comprises a mixtureof a compound of formula I wherein X is S and a benzotriazole UVabsorbing compound.
 29. The ophthalmic device of claim 23 wherein m andn in the compound of formula I at each occurrence are each
 0. 30. Theophthalmic device of any one of claim 23 wherein Y in the compound offormula I at each occurrence is independently alkylene, cycloalkylene,heterocycloalkylene, arylene, heteroarylene, oxaalkylene,alkylene-amide-alkylene, alkylene-amine-alkylene, or combinationsthereof.
 31. The ophthalmic device of claim 23 wherein R_(g) in thecompound of formula I at each occurrence independently comprises styryl,vinyl carbonate, vinyl ether, vinyl carbamate, N-vinyl lactam,N-vinylamide, (meth)acrylate, or (meth)acrylamide.
 32. The ophthalmicdevice of claim 20 wherein the ophthalmic device is a silicone hydrogelcontact lens, and wherein the silicone hydrogel contact lens has acontact angle of about 70° or less, a water content of at least 25percent, and an oxygen permeability of at least 80 barrers.
 33. Anophthalmic device that is a polymerized reaction product of a reactivemixture comprising a hydrophilic component, and a silicone containingcompound, wherein the polymerized reaction product contains, ascovalently bound substituents, one or more chromophores of formula IV:

wherein m and n are independently 0, 1, 2, 3, or 4; X is O, S, NR, SO,or SO₂; R at each occurrence is independently H, C₁-C₆ alkyl,cycloalkyl, heterocycloalkyl, aryl, heteroaryl, or a link to thepolymerized reaction product; R¹ and R², when present, are independentlyat each occurrence C₁-C₆ alkyl, C₁-C₆ alkoxy, C₁-C₆ thioalkyl, C₃-C₇cycloalkyl, aryl, halo, hydroxy, amino, NR³R⁴, or benzyl, wherein R³ andR⁴ are independently H or C₁-C₆ alkyl, or two adjacent R¹ or R² groups,together with the carbon atoms to which they are attached, combine toform a cycloalkyl or aryl ring; R⁵ is a link to the polymerized reactionproduct; and EWG is an electron withdrawing group.
 34. The ophthalmicdevice of claim 33 wherein X is O.
 35. The ophthalmic device of claim 34wherein X is S.
 36. The ophthalmic device of claim 33 wherein thepolymerized reaction product further comprises one or more UV absorbingchromophores covalently attached thereto.
 37. The ophthalmic device ofclaim 36 wherein the UV absorbing chromophore is the residue of abenzophenone, a benzotriazole, a triazine, a substituted acrylonitrile,a salicyclic acid derivative, a benzoic acid derivative, a cinnamic acidderivative, a chalcone derivative, a dypnone derivative, a crotonic acidderivative, or mixtures thereof.
 38. The ophthalmic device of claim 33wherein the link to the polymerized reaction product comprises theresidue of a polymerizable group and one or more of an alkylene group, acycloalkylene group, a heterocycloalkylene group, an arylene group, aheteroarylene group, an oxaalkylene group, an alkylene-amide-alkylenegroup, or an alkylene-amine-alkylene group.
 39. The ophthalmic device ofclaim 38 wherein the polymerizable group comprises styryl, vinylcarbonate, vinyl ether, vinyl carbamate, N-vinyl lactam, N-vinylamide,(meth)acrylate, or (meth)acrylamide.
 40. A silicone hydrogel contactlens that is a reaction product of a reactive mixture comprising: apolymerizable high energy light absorbing compound; and one or moremonomers suitable for making an ophthalmic device, wherein the contactlens has a contact angle of about 70° or less, a water content of atleast 25 percent, and an oxygen permeability of at least 80 barrers, andwherein the contact lens is substantially photostable.
 41. The siliconehydrogel contact lens of claim 40 wherein the lens transmits: from 1percent to 70 percent of light having a wavelength of 400 to 409 nm; andat least 80 percent of light having a wavelength of 450 to 800 nm. 42.The silicone hydrogel contact lens of claim 40, wherein thepolymerizable high energy light absorbing compound is a compound offormula I.
 43. The ophthalmic device of claim 23 wherein EWG is cyano.44. The ophthalmic device of claim 33 wherein EWG is cyano.
 45. Theophthalmic device of claim 42 wherein EWG is cyano.
 46. A siliconehydrogel formed from a reactive mixture comprising: a high energy lightabsorbing compound; between about 1 and about 15 wt % of at least onepolyamide; at least one first mono-functional, hydroxyl substitutedpoly(disubstituted siloxane) having 4 to 8 siloxane repeating units; atleast one second hydroxyl substituted poly(disubstituted siloxane) thatis a mono-functional hydroxyl substituted poly(disubstituted siloxane)having 10 to 200 siloxane repeating units; and about 5 to about 35 wt %of at least one hydrophilic monomer.
 47. The silicone hydrogel of claim46 wherein the high energy light absorbing compound is a compound offormula I.